《Table 1.Chemical composition of the SPL》

《Table 1.Chemical composition of the SPL》   提示：宽带有限、当前游客访问压缩模式
本系列图表出处文件名：随高清版一同展现
《Enhancement of the nickel converter slag-cleaning operation with the addition of spent potlining》


  1. 获取 高清版本忘记账户？点击这里登录
  1. 下载图表忘记账户？点击这里登录
wt%

According to its X-ray powder diffraction（XRD）analysis results（Fig.2），the as-received SPL from an aluminum smelter contained mainly graphite，Na F，nepheline（Na Al Si O4），Na2O（Al2O3）11，and silicon（Si）.Its chemical composition is listed in Table 1.The presence of Si is possibly due to the reduction of the siliceous refractory components in the highly reductive environment present in the Al electrolytic cells.

图表编号XD002875000    严禁用于非法目的
绘制时间2018.08.01
作者Dawei Yu、Kinnor Chattopadhyay
绘制单位School of Metallurgy and Environment,Central South University、Canmet MINING,Natural Resources Canada、Process Metallurgy & Modelling Group,Department of Materials Science and Engineering,University of Toronto
更多格式高清、无水印（增值服务）

相关图表

  1. 《Table 1.Chemical composition of the ZhS6U base metal》2019.02.01
  2. 《Table 1 Chemical composition of the investigated steel/wt》2019.02.01
  3. 《Table 1 Chemical composition of the experimental ingredients》2019.01.01
  4. 《Table 1 Chemical compositions of the studied alloys (wt%)》2019.01.01
  5. 《Table 1.Chemical composition and transformation temperatures of the studied TRIP steels》2019.01.01
  6. 《Table 1 Chemical composition of the alloy (wt%)》2018.11.01
  7. 《Table 1 Chemical composition of the alloys (wt%)》2018.11.01
  8. 《Table 1 Chemical composition of the marked areas in Fig.1》2018.10.01
  9. 《Table 1 Chemical composition of the alloy powders (wt%)》2018.09.01
  10. 《Table 1 Chemical composition of the test materials》2018.12.30
  11. 《Table 1 Chemical composition of the duplex stainless clad steel plate》2018.06.30
  12. 《Table 1 Chemical composition of the tested steel》2018.03.30
  13. 《Table 1.Chemical composition of the as-received Ti2AlN b-based alloy ingot at》2018.10.01
  14. 《Table 1.Chemical composition of the investigated pipe wt》2018.08.01
  15. 《Table 1.Chemical compositions of the tested steels》2018.08.01
  16. 《Table 1.Chemical composition of the HCVTM iron ore》2018.08.01
  17. 《Table 1.Chemical composition of the investigated material》2018.06.01
  18. 《Table 1.Chemical composition of the 316L stainless steel used in this study》2018.06.01
  19. 《Table 1.Chemical composition of the materials used》2018.05.01
  20. 《Table 1.Chemical compositions and production processes of the investigated steels》2018.03.01

随机翻阅

《表2 感官评分标准：基于等效实度法的直叶片垂直轴风力机风能利用系数分析》 《表1：旅游广播SWOT分析表》 《表4 灯控区与非灯控区槟榔坐果情况》 《表2 预设轧制工艺参数：大单重钼板热轧有限元模拟》 《表1 不同焦样光学组织组成的测定结果》 《表7 不同区域土壤重金属的潜在生态风险评价》 《表1 两组实习护生的理论考试成绩对比[（±s），分]》 《表2 对比两组住院时间与机械通气时间 (±s)》 《表3 碱激发矿渣净浆和碱激发矿渣陶砂砂浆的抗压强度Tab.3 Compressive strength of alkali-activated slag pastes and mortars》 《表2 两组患者的Harris功能评分比较 (±s)》