《Table 1 Chemical composition of the alloy powders (wt%)》

《Table 1 Chemical composition of the alloy powders (wt%)》   提示：宽带有限、当前游客访问压缩模式
本系列图表出处文件名：随高清版一同展现
《Si对MCrAlY涂层微观结构及性能的影响（英文）》


  1. 获取 高清版本忘记账户？点击这里登录
  1. 下载图表忘记账户？点击这里登录

Three kinds of Co Cr Al Y alloy powders with Si mass concentrations of 2%and 5%were designed and prepared by VIGA-16 vacuum atomization furnace in the study.Their chemical composition is listed in Table 1.The Co Cr Al Si Y coating，in a thickness about 0.2 mm，was prepared on a GH907substrate in a diameter of 22 mm by using GTV-K2 high velocity oxygen fuel apparatus.A constant oxidation test at 1050°C was performed in a muffle furnace.An automatic cycle thermal shock test machine was applied to investigate the coating thermal shock resistance at 1050°C.After keeping for 10 min in the high temperature test facility，the samples were taken out and quenched in（20±5）°C water for 1 min.For each thermal shock cycling step，the sample appearance was photographed.In addition，scanning electron microscopy（SEM）was used to gain knowledge of the micro structure and surface oxide film of the alloy powder and coatings.The distribution of different elements in the powders was analyzed by EDS.

图表编号XD0011262500    严禁用于非法目的
绘制时间2018.09.01
作者张淑婷、杜开平、任先京、史记
绘制单位北京矿冶研究总院、特种涂层材料与技术北京市重点试验室、北京市工业部件表面强化与修复工程技术研究中心、北京矿冶研究总院、特种涂层材料与技术北京市重点试验室、北京市工业部件表面强化与修复工程技术研究中心、北京矿冶研究总院、北京矿冶研究总院、特种涂层材料与技术北京市重点试验室、北京市工业部件表面强化与修复工程技术研究中心
更多格式高清、无水印（增值服务）

相关图表

  1. 《Table 1 Chemical compositions of Ti-5Al-5Mo-5V-1Cr-1Fe alloy (wt.%)》2019.02.01
  2. 《Table 1 Chemical compositions of Al-14Si-2Fe alloys with different Mn contents (wt.%)》2019.02.01
  3. 《Table 1 Chemical composition of Al-5.46wt.%Zn-1. 6 7 wt.%Mg alloy (mass fraction, %)》2019.02.01
  4. 《表1 5083铝合金的化学成分 (质量分数, %) Tab.1 The chemical composition of 5083aluminum alloy (wt%)》2019.01.25
  5. 《Table 1 Chemical composition of the investigated steel/wt》2019.02.01
  6. 《Table 1 Actual chemical compositions of the investigated alloys》2019.02.01
  7. 《Table 1 GH4169 alloy chemical composition (wt%)》2019.02.01
  8. 《Table 1 Chemical composition of base metals of TC4 and 2A14 alloys (wt%)》2019.01.01
  9. 《Table 1 Chemical compositions of the studied alloys (wt%)》2019.01.01
  10. 《表2 2024铝合金化学成分Table 2 Chemical composition of 2024 aluminium alloy (wt%)》2018.06.25
  11. 《Table 1 Chemical composition of the alloy (wt%)》2018.11.01
  12. 《Table 1 Chemical composition of the alloys (wt%)》2018.11.01
  13. 《Table 1 Chemical composition of A390 aluminum alloy (wt%)》2018.11.01
  14. 《Table 1 Chemical composition of 5A05 Al alloy (wt%)》2018.10.01
  15. 《Table 1 Nominal chemical compositions of Inconel718superalloy and powder (wt%)》2018.10.01
  16. 《Table 1 Chemical composition of as-cast AZ31 magnesium alloy (wt%)》2018.10.01
  17. 《Table 1 Chemical composition of Mg-5.9Zn-1.6Zr-1.6Nd-0.9Y alloy (wt%)》2018.05.01
  18. 《Table 1 Chemical composition of Ag-Cu-Ti fillers alloy (wt%)》2018.04.01
  19. 《Table 1 Chemical composition of ADC12 alloy (wt%)》2018.03.01
  20. 《Table 1.Chemical composition of the investigated pipe wt》2018.08.01

随机翻阅

《表3 定量分析表：基于建模思想的“一元一次方程应用”教学的思考》 《表1 大学生炫耀性消费部分测量题项》 《表5 沥青稳定碎石矿料级配》 《表1 术后并发症发生率的对比 (n, %)》 《表2 一次应力校核汇总表》 《表6 安慰剂检验回归：股息税差别化征收与公司分红——基于DID模型的实证研究》 《表2 两组病例术中及术后情况》 《表2 不同厂址含氚硝酸和水复用数据对比表 (按每吨铀计)》 《表1 试卷质量分析体系：基于大学数学教学改革的试卷分析评价体系的建立与实践》 《表1 论文发表的期刊种类及篇数》