《Table 1.Chemical compositions of the tested steels》
提示：宽带有限、当前游客访问压缩模式
本系列图表出处文件名：随高清版一同展现
《Effect of Nb and V on the continuous cooling transformation of undercooled austenite in Cr–Mo–V steel for brake discs》
wt%
The compositions of the tested steels are shown in Table1.Steel A is the basic steel，whereas steels B and C have a higher V content and a higher Nb content compared with steel A，respectively.The size of cylindrical specimens was?4 mm×10 mm，and the process tests were conducted on a thermal dilatometer（DLC805L）.The phase transformations at different cooling rates were studied.The heating schedule is illustrated in Fig.1.