《Table 1.Chemical composition of the ZhS6U base metal》
提示:宽带有限、当前游客访问压缩模式
本系列图表出处文件名:随高清版一同展现
《Weldability and liquation cracking behavior of ZhS6U superalloy during electron-beam welding》
wt%
Fig.2 illustrates a non-heat-treated microstructure coupon in which the light phase and the needle-shaped carbide in the matrix phase(γphase andγ′precipitates,respectively)are visible.The energy dispersive spectroscopy(EDS)analysis results for point A(Fig.2)are presented in Table 2.These results indicate that MC carbides are present in the microstructure.During the service time of the superalloy under high temperature,these carbides did not transform to M23C6 and M6C carbides.
图表编号 | XD0050013300 严禁用于非法目的 |
---|---|
绘制时间 | 2019.02.01 |
作者 | Arash Khakzadshahandashti、Mohammad Reza Rahimipour、Kourosh Shirvani、Mansour Razavi |
绘制单位 | Department of Ceramic,Materials and Energy Research Center、Department of Ceramic,Materials and Energy Research Center、Department of Material and Renewal Energy, Iranian Research Organization for Science and Technology (IROST)、Department of Ceramic,Materia |
更多格式 | 高清、无水印(增值服务) |