《Table 1 Crystal parameters of PPTA with different inherent viscosities》
本系列图表出处文件名:随高清版一同展现
《Kinetics Analysis on the Polycondensation Process of Poly(p-phenylene terephthalamide):Experimental Verification and Molecular Simulation》
Based on the optimal conditions as mentioned above,PPTA samples with different inherent viscosities were obtained by the twin screw.The detailed technological parameters for each reaction step within the twin screw will be discussed in another article.In the present study,microstructure parameters of the prepared PPTA resin were investigated by X-ray diffraction technique.An X-ray beam directed perpendicularly to the axis produced reflections from layer planes.The Scherrer equation was used to calculate the stacking height of layer planes in vertical direction of the crystal.Figure 4 presents equatorial X-ray diffraction patterns of PPTA with different inherent viscosities recorded at room temperature.Qualitative inspection of equatorial X-ray diffraction patterns showed three sharp peaks at about 2θ=20.9°(d=0.42 nm),2θ=23.6°(d=0.39 nm)and 2θ=28.5°(d=0.31 nm),which could be indexed as(110),(200) and(004)diffractions,respectively[36,37].Crystal parameters obtained from equatorial X-ray diffraction patterns are given in Table 1.It indicates that the crystallinity increased with the inherent viscosity but the stacking size(D)of PPTA was almost invariable even with different inherent viscosities and crystallinities.
图表编号 | XD0020170000 严禁用于非法目的 |
---|---|
绘制时间 | 2018.05.01 |
作者 | Jing Liu、Hai-Juan Kong、Yu Ma、Shu Zhu、Mu-Huo Yu |
绘制单位 | State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, College of Materials Science and Engineering, Donghua University、School of Materials Engineering, Shanghai University of Engineering Science、State Key Laboratory for Modificat |
更多格式 | 高清、无水印(增值服务) |
查看“Table 1 Crystal parameters of PPTA with different inherent viscosities”的人还看了
- Table 1–Surface area (SBET) and porosity parameters of Bi2MoO6/ZnInAl-CLDH with different C contents.