《Table 1 Experimental value for K (φ) of the specimens annealed at 673 K and their ratio to the valu
提示:宽带有限、当前游客访问压缩模式
本系列图表出处文件名:随高清版一同展现
《高能球磨制备Al-Pb纳米相复合结构合金中纳米相Pb体积分数对其长大行为影响(英文)》
In Fig.6,it is apparent that the value of coarsening rate of Pb nanophase increases significantly as the volume fraction increases under the same heating condition.In other words,the volume fraction of Pb nanophase in Al-Pb nanocomposite alloys has an obvious effect on the coarsening of Pb nanophase.Table 1 shows that K(φ)increases with increasing Pb nanophase volume fraction.This result is the most direct evidence that the coarsening in this system is controlled by diffusion.The observed increase of K(φ)withφis more rapid than that predicted by Ardell[11],Brailsford and Wynblatt[12]in this composition range.
图表编号 | XD0011250900 严禁用于非法目的 |
---|---|
绘制时间 | 2018.07.01 |
作者 | 吴志方、吴江、张磊、吴润、常庆明 |
绘制单位 | 武汉科技大学省部共建耐火材料与冶金国家重点实验室、武汉科技大学省部共建耐火材料与冶金国家重点实验室、武汉科技大学省部共建耐火材料与冶金国家重点实验室、武汉科技大学省部共建耐火材料与冶金国家重点实验室、武汉科技大学省部共建耐火材料与冶金国家重点实验室 |
更多格式 | 高清、无水印(增值服务) |
查看“Table 1 Experimental value for K (φ) of the specimens annealed at 673 K and their ratio to the value of Al-0.33vol%Pb co”的人还看了