《Table 2.Experimental scheme for the smelting separations of HVTMP》

《Table 2.Experimental scheme for the smelting separations of HVTMP》   提示：宽带有限、当前游客访问压缩模式
本系列图表出处文件名：随高清版一同展现
《Effects of smelting parameters on the slag/metal separation behaviors of Hongge vanadium-bearing titanomagnetite metallized pellets obtained from the gas-based direct reduction process》


  1. 获取 高清版本忘记账户？点击这里登录
  1. 下载图表忘记账户？点击这里登录
*:Experimental conditions of No.2，No.7，No.13 and No.19 are the basic smelting parameters.

In the experiments，the effects of smelting temperature，smelting time，C/O ratio，and Ca O/Si O2 ratio were investigated.These parameters were 1823–1898 K，10–60 min，0.70–1.50，and 0.18–0.80，respectively.When the smelting Ca O/Si O2 ratio was 0.18，the Ca O fluxes were not added.In this study，the single-factor control variable method，in which only a single parameter was changed and the other parameters were maintained under the basic conditions，was used to investigate the effects of various smelting parameters on the recovery of valuable elements in the smelting separation process of HVTMP.The basic smelting parameters were a smelting temperature of 1848 K，a smelting time of 30 min，a C/O ratio of 1.10，and a Ca O/Si O2 ratio of 0.60.The detailed experimental scheme is shown in Table 2.

图表编号XD002870400    严禁用于非法目的
绘制时间2018.06.01
作者Cong Feng、Man-sheng Chu、Jue Tang、Zheng-gen Liu
绘制单位School of Metallurgy, Northeastern University、School of Metallurgy, Northeastern University、School of Metallurgy, Northeastern University、School of Metallurgy, Northeastern University
更多格式高清、无水印（增值服务）

相关图表

  1. 《Table 2 Scheme for optimization of land use structure in the districts of Hohhot》2018.11.01
  2. 《Table 1 Experiment scheme for the interaction treatment》2018.07.01
  3. 《Table 2 Scheme of the strategy transformation regionalization for Ningxia ACD[16]》2019.06.25
  4. 《表2 摇床分选实验结果Tab.2 Experimental results of shaking table separation》2019.02.25
  5. 《Table 2.Experimental scheme for fluid diversion ability evaluation.》2019.02.01
  6. 《Table 3 The IRSN schemes of the Tangxun Lake group》2019.03.01
  7. 《Table 2 Influence of different percentages of alkaline additives on the chiral separation of dihydropyridine calcium ant》2019.02.20
  8. 《表1 试验豆粉溶液方案Tab.1 The scheme of soybean solution for testing》2019.01.15
  9. 《Table 1 Separations of racemates on the M1-coated column*》2019.02.10
  10. 《Table 2 Influence of the saponification degree of D2EHDTPA on the separation factor*》2019.01.10
  11. 《Table 1 Experimental scheme for optimization of electrokinetic remediation conditions》2019.02.01
  12. 《表2 阻力计算的分相流模型评价Tab.2 Evaluation of different separated flow models for cal-culating the frictional pressure drop》2018.05.15
  13. 《Table 2 MRE of the compared methods for two numbers of samples (schemes 14 and 19)》2018.03.01
  14. 《Table 2 Experimental schemes of deep cryogenic treatment》2018.10.01
  15. 《表2 Co Cr Al Y涂层的喷丸强化实验方案Table 2 Experimental schemes of Co Cr Al Y coating shot peening》2018.09.01
  16. 《表2 沥青的冻融循环方案Table 2 Scheme of salt-freezing cycles for the test asphalt》2018.06.25
  17. 《表2 空箱抗压试验数据Table 2 Experimental data of the compressive test for empty corrugated box》2018.03.01
  18. 《Table 1.Chemical compositions of HVTMP》2018.06.01
  19. 《Table 1.Results of the flotation separation of chalcopy-rite–galena artificial mixed minerals》2018.05.01
  20. 《Table 2–Experimental parameters of BBD and the degree for succinylation.》2018.07.01

随机翻阅

《表4 五类人群梅毒和HIV感染情况[n(%)]》 《表2 注入水参数：低渗透砂砾岩油藏水敏伤害机理及注入水水源优选》 《表2 京津风沙治理工程2018年工程区与非工程区对比》 《表2 LM、HA及APRI诊断肝纤维化的诊断价值》 《表1 脐带血PCT、IL-6、CRP对SBI诊断价值》 《表1 两组患者再次宫腔粘连及程度情况比较[n（%）]》 《表3 毛泽东思想的形成和发展阶段》 《表5 3种方法异常值剔除时间和错误概率比较Tab 5 Comparison of outlier elimination time and error rate of 3 methods》 《表6 婚前同居接受程度调查表》 《表5 两组手术前后血清神经损伤分子含量比较 (±s)》