《Table 1 The mass percentage of HNTs and PDMS reinforced coating formulations》
提示:宽带有限、当前游客访问压缩模式
本系列图表出处文件名:随高清版一同展现
《Effects of Halloysite Nanotube Reinforcement in Expandable Graphite Based Intumescent Fire Retardant Coatings Developed Using Hybrid Epoxy Binder System》
First,epoxy(BPA)resin was heated for 15 min at 50°C to be prepared for PDMS incorporation.Preheated epoxy(BPA)resin and PDMS in 3:2(W:W)were taken into a flask fitted with a thermometer and magnetic stirrer.The reaction mixture was continuously stirred at 45°C for 15 min.All intumescent ingredients,except curing agent,polyamide,were ground for 1 min to homogenize using a grinder(Table 1).
图表编号 | XD0020173100 严禁用于非法目的 |
---|---|
绘制时间 | 2018.11.01 |
作者 | Qandeel Fatima Gillani、Faiz Ahmad、M.I.Abdul Mutalib、Puteri S.M.Megat-Yusoff、Sami Ullah |
绘制单位 | Mechanical Engineering Department, Universiti Teknologi PETRONAS、Mechanical Engineering Department, Universiti Teknologi PETRONAS、Chemical Engineering Department, Universiti Teknologi PETRONAS、Mechanical Engineering Department, Universiti Teknologi PETRON |
更多格式 | 高清、无水印(增值服务) |
查看“Table 1 The mass percentage of HNTs and PDMS reinforced coating formulations”的人还看了
- Table 2 The percentage of the Singapore Chinese using English and Chinese dialects in different communicative context (%
- Table 3 The percentage of the Singapore Chinese using English and Mandarin in government organizations and shopping cent