《Table 3 Elemental compositions and XPS analysis of HNTs》

《Table 3 Elemental compositions and XPS analysis of HNTs》   提示：宽带有限、当前游客访问压缩模式
本系列图表出处文件名：随高清版一同展现
《Effects of Halloysite Nanotube Reinforcement in Expandable Graphite Based Intumescent Fire Retardant Coatings Developed Using Hybrid Epoxy Binder System》


  1. 获取 高清版本忘记账户？点击这里登录
  1. 下载图表忘记账户？点击这里登录

In order to analyse the elemental composition present in the char residue，XPS analysis of SH formulation was conducted and results are presented in Table 3.

图表编号XD0020173000    严禁用于非法目的
绘制时间2018.11.01
作者Qandeel Fatima Gillani、Faiz Ahmad、M.I.Abdul Mutalib、Puteri S.M.Megat-Yusoff、Sami Ullah
绘制单位Mechanical Engineering Department, Universiti Teknologi PETRONAS、Mechanical Engineering Department, Universiti Teknologi PETRONAS、Chemical Engineering Department, Universiti Teknologi PETRONAS、Mechanical Engineering Department, Universiti Teknologi PETRON
更多格式高清、无水印（增值服务）

相关图表

  1. 《Table1 Elemental analysis results of acrylated avermectin and emulsifier precursor》2019.05.10
  2. 《Table 4.Surface elemental composition of Ce and Zr in different catalysts deter-mined by XPS.》2019.01.01
  3. 《Table 3–Surface composition and oxidation state of Fe2p species over CuFe-SSZ-13 catalysts from XPS analyses.》2019.07.15
  4. 《Table 1–Chemical elemental analysis of ARPOP and PI-b-ARPOP.》2019.04.15
  5. 《Table 2 Elemental analysis data of k-CM, k-CM/APP (2/1) , k-CM/APP (3/1) and k-CM/APP (4/1)》2019.02.10
  6. 《表4 催化剂表层元素XPS分析结果Table 4 Surface compositions of catalysts from XPS analysis》2018.03.30
  7. 《表2 燃煤的工业分析和元素分析/%Table 2 Industrial and elemental analysis of coal for the tested boilers》2018.04.15
  8. 《Table 3–The surface elemental composition of biochars at the hydrothermal temperature of 140°C, hydrothermal time of8 hr》2018.11.15
  9. 《Table 1 Elemental analysis results of composite antioxidants》2018.09.15
  10. 《表4 1, 2和3的元素分析Table 4 Elemental analysis data of 1, 2 and 3》2018.07.20
  11. 《表3 多孔炭各元素的原子分数Table 3Comparison of the elemental composition of porous carbons》2018.05.30
  12. 《Table 2 Elemental surface composition of CNC-Br and CNC-PDMAEMA, as determined by XPS》2018.10.01
  13. 《Table 1 Appearance, yields and elemental analysis data of new compounds involved》2018.04.10
  14. 《Table 3 Elemental analysis of Mt, STAC-Mt and FMC》2018.02.10
  15. 《表1 石墨毡处理前后的XPS表面元素分析Tab.1 XPS surface elemental analysis parameters of the untreated and treated GFs》2018.02.25
  16. 《表2 样品1及阴离子交换样品的元素分析结果和化学计量式Table 2 Elemental analysis results of Sample 1 and those anion-exchanged and their stoichiome》2018.06.25
  17. 《Table 3 Elemental analysis of fresh, spent and HI-regenerated catalyst samples》2018.06.30
  18. 《Table 1 Elemental analysis of PIL-a3 and PIL-b3》2018.06.30
  19. 《Table 1 The chemical composition of HNTs》2018.03.30
  20. 《Table 3 Elemental composition of bimetallic catalysts by XRF analysis》2018.03.30

随机翻阅

《表3 两组间受精率和优质胚胎率比较（±s，个）》 《表4 湖北栲类林种子植物的区系成分》 《表1 两组患者ICU住院时间、症状缓解时间、胃肠功能恢复时间、体征稳定时间比较(±s,d)》 《表1 两组疗效比较：药物联合治疗精神分裂症的效果及不良反应》 《表1 环境规制与制造业产业集聚得到影响：门槛变量自抽样检验》 《表1 新建道路场区内土层参数 (1)》 《表1 2组患者治疗前后血清PAF含量比较（±s)》 《表2 颖神星轨道参数 (MJD=58000.0)》 《表1 绩效期望的测量问题》 《表1 非渗油蠕变橡胶防水涂料的主要性能》