《Table 2 Elemental surface composition of CNC-Br and CNC-PDMAEMA, as determined by XPS》
本系列图表出处文件名:随高清版一同展现
《Functionally Modified Cellulose Nanocrystals as an Adsorbent for Anionic Dyes》
FT-IR and XPS analyses were carried out to examine the chemical structure and surface elements of CNC-Br and CNC-PDMAEMA.BIBB was anchored on the surface of CNC by esterification to prepare the ATRP initiator.As shown in Fig.1(b),unlike CNC,CNC-Br showed a strong FT-IR peak at 1740 cm-1.This peak corresponds to the stretching vibration of C=O from the ester group[19].A strong peak at 1280 cm-1 corresponding to C—O was observed in the FT-IR spectrum of CNC-Br(Fig.1 (b)) [20].The XPS spectrum of CNC-Br(Fig.2)showed a Br3d peak at 68 eV.It can be observed from Table 2 that the Br content in CNC-Br was 3.01%.These results suggest that BIBB was successfully grafted onto the CNC surface(reaction is shown in Scheme 1).
图表编号 | XD0020754600 严禁用于非法目的 |
---|---|
绘制时间 | 2018.10.01 |
作者 | Ming Li、ShiYu Fu |
绘制单位 | State Key Laboratory of Pulp and Paper Engineering, South China University of Technology、State Key Laboratory of Pulp and Paper Engineering, South China University of Technology |
更多格式 | 高清、无水印(增值服务) |
查看“Table 2 Elemental surface composition of CNC-Br and CNC-PDMAEMA, as determined by XPS”的人还看了
- Table 3–Surface composition and oxidation state of Fe2p species over CuFe-SSZ-13 catalysts from XPS analyses.