《Table 2–Fiber morphology of the electrospun copolymer nanofibers.》
本系列图表出处文件名:随高清版一同展现
《Preparation of glutinous rice starch/polyvinyl alcohol copolymer electrospun fibers for using as a drug delivery carrier》
SEM characteristics of GRS-PVA electrospun fibers are illustrated in Fig.2 and fiber diameter sizes of each formulation were reported in Table 2.The smooth fibers were obtained at PVA concentration from 8%to 10%(w/v).At 5%PVA(w/v),it was not possible to obtain smooth fibers,as seen in Fig.2A-C.They are beaded fibers in which similar to the findings from Supaphol and Chuangchote[20].The GRS-PVA nanofibers that contain 8%PVA(w/v)with 1–3%GRS(w/v)formed smooth fibers with an average diameter of 191–263 nm as shown in Fig.2D-F.The copolymer nanofibers of 10%PVA(w/v)with 1and 2%GRS(w/v)also formed smooth fibers,but they demonstrated a larger fibrous diameter than the copolymer nanofibers of 8%PVA(w/v)with 1–3%GRS(w/v).On the other hand,increasing GRS to 3%(w/v)with 10%(w/v)PVA was not possible to fabricate the nanofibers because the solution possessed a high viscosity.Consequently,it led to a clogging at the tip of the needle which impedes electrospinning process.Starch has been reported as detrimental to an electro spinnability of polymer blends[28].
图表编号 | XD00186264300 严禁用于非法目的 |
---|---|
绘制时间 | 2018.05.01 |
作者 | Patthanakorn Jaiturong、Busaban Sirithunyalug、Sukum Eitsayeam、Chawalinee Asawahame、Pratchaya Tipduangta、Jakkapan Sirithunyalug |
绘制单位 | Department of Pharmaceutical Sciences, Faculty of Pharmacy, Chiang Mai University、Department of Pharmaceutical Sciences, Faculty of Pharmacy, Chiang Mai University、Department of Physics and Materials, Faculty of Science, Chiang Mai University、Department o |
更多格式 | 高清、无水印(增值服务) |