《Table 4 EDS results of the areas marked in Fig.8 (at%)》
本系列图表出处文件名:随高清版一同展现
《pH值对镁合金表面水热沉积磷酸钙涂层微观形貌和腐蚀性能的影响(英文)》
Fig.8 shows the SEM micrographs of the specimens.The chemical components of the corresponding areas in Fig.8obtained by EDS are listed in Table 4.Fig.8a shows that the naked AZ31 is covered by a reaction layer and lots of cracks are found on the surface.Table 4 shows that besides Mg and O,significantly high contents of P(7.18 at%)and Ca(6.11 at%)on area 1 are detected,which means that calcium phosphate is formed while the Mg substrate is corroded.Specimens treated at pH=6 and pH=10 show that most of the coating are intact except a very small part of the coating damaged(marked in area 2 and area 6).EDS results on these damaged areas show a significantly high contents of P and Ca compare with the substrate(area 1).The reason may be that there is an ionic bond of Mg2+and PO43–at the interface between the initial sediments and the AZ31 substrate,which will cause a strong combination of the inner calcium phosphate layer.Fig.8c shows the corrosion spots of the pH=8-treated specimen(marked in Fig.7c),suggesting that part of the HA layer has fallen off and a large amount of Mg(21.26 at%)and 1.76 at%Al are detected(marked in area 4).
图表编号 | XD0011273700 严禁用于非法目的 |
---|---|
绘制时间 | 2018.10.01 |
作者 | 张春艳、张世雨、柳歆鹏、何洪川 |
绘制单位 | 重庆理工大学、重庆市特种焊接材料与技术高校工程研究中心、重庆理工大学、重庆理工大学、重庆理工大学 |
更多格式 | 高清、无水印(增值服务) |
查看“Table 4 EDS results of the areas marked in Fig.8 (at%)”的人还看了
- Table 3–Fitting results of the impedance spectra shown in Fig.8 obtained in the AEM systems according to the equivalent