《Table 2:Environment-sensitive embedding energy of Zn, Mg, Cu at grain boundary and inα-Al (eV) [21]
本系列图表出处文件名:随高清版一同展现
《Microstructural evaluation and mechanical properties of 7075 aluminum alloy prepared by controlled diffusion solidification》
The scanning data of the primaryα-Al phases and the eutectic phases of the CC and the CDS(Fig.7)samples are shown in Table 3.It is discernible that the amount of Al atoms decreases gradually from the center of the primaryα-Al phases to the eutectic phases,whereas the contents of Zn,Mg,and Cu atoms increase gradually from the center of the primaryα-Al phases to the eutectic phases.Moreover,the contents of Zn,Mg,and Cu atoms in the eutectic phases of the CDS sample(point D1)are found to be higher than those in the eutectic phases of the CC sample(point D).However,at the center of the primaryα-Al phases,the amounts of Zn,Mg,and Cu atoms in the CDS sample(point A1)are lower than those in the CC sample(point A).Furthermore,at the boundary of the primaryα-Al phases,the contents of Zn,Mg,and Cu atoms in the CDS sample(point C1)are higher than those in the CC sample(point C).
图表编号 | XD0088361800 严禁用于非法目的 |
---|---|
绘制时间 | 2019.07.01 |
作者 | Xiong Yang、Yuan-dong Li、Xiao-mei Luo、Hong-wei Zhou、Qi-yong Cai、Ming Li、Ying Ma |
绘制单位 | State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou University of Technology、State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou University of Technology、State Key Laboratory of Adv |
更多格式 | 高清、无水印(增值服务) |