《Table 1 Tensile properties of as-extruded Mg-Zn-Ce alloys》

《Table 1 Tensile properties of as-extruded Mg-Zn-Ce alloys》   提示：宽带有限、当前游客访问压缩模式
本系列图表出处文件名：随高清版一同展现
《"Microstructures and Tensile Properties of Hot-extruded Mg-6Zn-xCe(x=0,0.6,1.0,2.0) Alloys"》


  1. 获取 高清版本忘记账户？点击这里登录
  1. 下载图表忘记账户？点击这里登录

The mechanical property test results（Table 1）revealed that a small amount of Ce had significant effect on tensile strength of Mg-6Zn alloy.With 0.6%Ce addition，the improvements of yield strength（YS）and ultimate tensile strength（UTS）were about 24MPa and 15 MPa，respectively.However，with further increasing Ce content，the YS and UTS were decreased slightly.It is noted that the differences of YS and UTS between Mg-6Zn-0.6Ce and Mg-6Zn-1Ce was less than 5 MPa.Mg-6Zn alloy without Ce addition showed good ductility，and the elongation was decreased with increasing Ce content.

图表编号XD0043328300    严禁用于非法目的
绘制时间2019.02.01
作者于合帅、杨文朋、CUI Hongbao、GUO Xuefeng、WANG Ying、WU Yali
绘制单位School of Materials Science and Engineering, Henan Polytechnic University、School of Materials Science and Engineering, Henan Polytechnic University、Henan International Joint Research Laboratory for High-Performance Light Metallic Materials and Numerical S
更多格式高清、无水印（增值服务）

相关图表

  1. 《Table 4.The tensile properties of the alloy under different processes》2019.02.01
  2. 《表3 7020铝合金常温拉伸性能Tab.3 Normal Temperature Tensile Properties of 7020 Aluminum Alloy》2019.04.20
  3. 《Table 3 EDS results of the as-extruded alloys》2019.02.01
  4. 《表1 TC25G钛合金整体叶盘室温拉伸性能Tab.1 Room-temperature tensile properties of TC25G titanium alloy blisk》2019.01.10
  5. 《表2 TC25G钛合金整体叶盘550℃拉伸性能Tab.2 Tensile properties of TC25G titanium alloy blisk at 550℃》2019.01.10
  6. 《表2 合金拉伸力学性能及IPA Tab.2 Tensile mechanical properties and IPA index of the alloys》2018.12.25
  7. 《表3 合金拉伸力学性能及IPA Tab.3 Tensile mechanical properties and IPA index of the alloys》2018.06.25
  8. 《表4 铝合金抗拉强度的方差分析Table 4 Variance analysis of tensile strength of aluminum alloy》2018.08.20
  9. 《表2 不同碳含量FGH4169合金的拉伸性能Table 2 Tensile properties of FGH4169 alloy with different carbon contents》2018.08.01
  10. 《表2 TC6钛合金精密锻造叶片高温拉伸性能Table 2 Tensile properties of precision forging blade for TC6 titanium alloy at high temperature》2018.07.25
  11. 《表2 TC4-DT钛合金锻件拉伸性能测试结果Table 2 Tensile properties results of TC4-DT titanium alloy forgings》2018.05.25
  12. 《Table 1 Average values of tensile properties of the w ool samples》2018.12.31
  13. 《Table 1 Transverse tensile properties of the alloy at different temperatures》2018.10.01
  14. 《Table 1 Tensile properties of the Mg-6Gd-4Y and Mg-6Gd-4Y-1Zn alloy at room temperature》2018.10.01
  15. 《表2 试验材料拉伸性能Table 2 Tensile properties of test materials》2018.06.15
  16. 《Table 3 Tensile properties of the welded joints》2018.09.30
  17. 《Table 2 Tensile properties of BW300TP》2018.06.30
  18. 《Table 4 Tensile properties of the welded joints》2018.06.30
  19. 《Table 3 Tensile properties of samples》2018.03.30
  20. 《Table 3.Tensile properties of investigated steels》2018.10.01

随机翻阅

《表3 新旧标准其他测试项目技术修改情况》 《表1 二氧化碳排放因子/（kg CO2/千克标准煤）》 《表1 两组产妇盆底肌电活动和盆底肌疲劳度对比[n,±s]》 《表2 拟合直线参数表：基于激光三角法的汽车同步带齿形轮廓参数测量》 《表5 管片混凝土物理力学参数取值》 《表2 KMO和巴特利特检验》 《表2 不同浓度清洗剂的清洗能力》 《表3 药物四气、五味分布》 《表1 1 Group Statistics》 《表1 两组患者肘关节Mayo评分（分，±s)》