《Table 3 Tensile properties of samples》
本系列图表出处文件名:随高清版一同展现
《The effect of cooling rate and coiling temperature on the microstructure and mechanical properties of a plain carbon steel》
Tensile experiments w ere performed at room temperature according to the national standard GB/T228.1-2010,and the results are show n in Table 3.Based on the results of samples S1,S2,and S3,the conventionally tested steel show ed a yield strength of 387 M Pa,a tensile strength of 531 M Pa,and an elongation of 24.3%w hen the coiling temperature is580℃.These properties slightly change for the IC sample.How ever,compared w ith LC,yield strength and tensile strength w ere improved about 137 and85 M Pa,respectively,w hile the elongation w as decreased by only 2 percentage points for UFC.Comparing the results betw een sample S3 and S4reveals that the yield strength and tensile strength of the steel plate increased to 608 and 682 M Pa,and the elongation reduced to 15.8%w hen the coiling temperature w as reduced from 580 to 500℃at a cooling rate of 120 K/s through UFC.
图表编号 | XD004630900 严禁用于非法目的 |
---|---|
绘制时间 | 2018.03.30 |
作者 | ZHANG Chen、HU Xiaoping、LIU Gang、WANG Huanrong |
绘制单位 | Research Institute,Baoshan Iron & Steel Co.,Ltd.、Research Institute,Baoshan Iron & Steel Co.,Ltd.、Research Institute,Baoshan Iron & Steel Co.,Ltd.、Research Institute,Baoshan Iron & Steel Co.,Ltd. |
更多格式 | 高清、无水印(增值服务) |