《Table 1 Transverse tensile properties of the alloy at different temperatures》
本系列图表出处文件名:随高清版一同展现
《一种镍基第三代单晶高温合金的横向拉伸性能(英文)》
Table 1 lists the transverse tensile properties of the alloy at760,850 980,1070 and 1100°C.Relationships between the transverse tensile properties of the alloy and temperatures are shown in Fig.2.The error bars denote their standard deviation.The results show that the yield strength(YS)of the alloy decreases as the temperature increases,and it decreases faster when the temperature is above 980°C.The ultimate tensile strength(UTS)of the alloy decreases as the temperature increases in the temperature range of 850°C to 1100°C.However,the elongation of the alloy increases with the temperature increasing,and the elongations at 1070 and1100°C are almost the same.That is to say,the transverse tensile strength is the highest and the transverse tensile elongation is relatively low at the medium temperature.With the increasing of temperature,the transverse tensile strength becomes lower and the transverse tensile elongation becomes higher.
图表编号 | XD0011272600 严禁用于非法目的 |
---|---|
绘制时间 | 2018.10.01 |
作者 | 杨万鹏、李嘉荣、刘世忠、史振学、赵金乾、王效光 |
绘制单位 | 北京航空材料研究院先进高温结构材料重点实验室、北京航空材料研究院先进高温结构材料重点实验室、北京航空材料研究院先进高温结构材料重点实验室、北京航空材料研究院先进高温结构材料重点实验室、北京航空材料研究院先进高温结构材料重点实验室、北京航空材料研究院先进高温结构材料重点实验室 |
更多格式 | 高清、无水印(增值服务) |