《Table 3 Mechanical properties of different samples obtained from bending tests》
本系列图表出处文件名:随高清版一同展现
《Preparation and Characterization of DGEBA/EPN Epoxy Blends with Improved Fracture Toughness》
For epoxy blend samples,the gradual incorporation of E1L0 epoxy into E0L1 epoxy up to blend containing 40%E1L0 epoxy gradually improved the ductility of the resulting material.Further increase in E1L0 fraction in the blend reduced the material’s ductility to the level of E1L0 sample.The blend composition dependence of flexural strength also follows the same trend as that observed for the strain at break.It is interesting to observe that the E4L6,E6L4 and E8L2blend samples show bending ductility higher than that of the neat E1L0 sample.A synergistic effect of the blending process on the material’s ductility can be observed in these samples.This improved ductility comes from the microstructure of these blend samples.The flexural data obtained from the stress-strain curves are depicted in Table 3.
图表编号 | XD0020168700 严禁用于非法目的 |
---|---|
绘制时间 | 2018.05.01 |
作者 | Morteza Khalina、Mohammad Hosain Beheshty、Ali Salimi |
绘制单位 | Department of Composites, Iran Polymer and Petrochemical Institute、Department of Composites, Iran Polymer and Petrochemical Institute、Department of Resin and Adhesives, Iran Polymer and Petrochemical Institute |
更多格式 | 高清、无水印(增值服务) |