《Table 2.EDS elemental analysis results for different areas of Cu foams》
提示:宽带有限、当前游客访问压缩模式
本系列图表出处文件名:随高清版一同展现
《Synthesis and characterization of copper foams through a powder metallurgy route using a compressible and lubricant space-holder material》
wt%
To investigate the impurities that might have been left behind after evaporation of the acrawax,we conducted EDS analysis of the foams.Fig.8 shows two EDS spectra corresponding to the point on the cell wall and the other at the pore periphery.Here,no impurities were present except for some oxidation(Table 2).The oxidation was less extensive in the cell wall regions and only slightly more extensive at the pore periphery.We therefore concluded from the EDS results that acrawax was volatilized completely without leaving any impurities within the metal foam matrix.
图表编号 | XD002875800 严禁用于非法目的 |
---|---|
绘制时间 | 2018.08.01 |
作者 | Mohit Sharma、O.P.Modi、Punit Kumar |
绘制单位 | Department of Mechanical Engineering,National Institute of Technology、CSIR-Advanced Materials & Processes Research Institute、CSIR-Advanced Materials & Processes Research Institute、Department of Material Science & Metallurgical Engineering,Maulana Azad Nat |
更多格式 | 高清、无水印(增值服务) |