《Tab.1 Assignment of IR and Raman spectra in KTm0.1-Yb0.9 (WO4) 2crystal》
It can be seen from Fig.4 that the infrared absorption peak of the crystal at 474 cm-1indicates the wagging vibration of WO4group,and the infrared absorption peaks at 636,771,840,889,926 cm-1can be attributed to the stretching vibration of WO4group.When the sample was placed in the air,some water came into the sample,so the infrared absorption peaks at 1 642 cm-1(1 469 cm-1)and3 461 cm-1are due to the bending vibration and asymmetric stretching of the O—H bond.The Raman spectrum of the crystal can be seen in Fig.5.The stronger Raman peaks at 84,109,199,346,413,681,761,802,899 cm-1and the weaker red light at 650 nm were observed,which indicates the crystal has multiple bonds with high-covalency.Tab.1 lists the vibration frequencies assignment of the crystal as for IR and Raman spectra.The results demonstrate the existence of the double oxygen bridge(WOOW)and the single oxygen bridge(WOW)in the crystal.
图表编号 | XD0017626400 严禁用于非法目的 |
---|---|
绘制时间 | 2018.04.01 |
作者 | 毕琳、底晓强、赵建平、李春、刘景和 |
绘制单位 | 长春理工大学计算机科学技术学院、长春理工大学计算机科学技术学院、长春理工大学计算机科学技术学院、长春理工大学材料科学与工程学院、长春理工大学材料科学与工程学院 |
更多格式 | 高清、无水印(增值服务) |