《Table 2 TGA and DTG data of PET fibers》
本系列图表出处文件名:随高清版一同展现
《Preparation and Properties of Poly(ethylene terephthalate )(PET) Coated by Chitosan( CS) Based on Sol-gel Method》
aInitial decomposition temperature;bThe maximum decomposition temperature,corresponding to the temperature peak in the DTG curves
Thermal behaviors of pristine and modified PET fibers w ere investigated by thermogravimetric analysis(TGA).Figure 7show s the TGA and differential thermal gravity(DTG)curves of pristine PET,hydrolyzed PET,SE-PET and CS-SE-PET fiber.It is easy to notice that all TGA and DGT curves manifest identical trend,indicating that SE and CS slightly affect thermal decomposition mechanism of PET matrix.From Fig.7(a),there is an obvious weight loss in the range of 400 550℃,which can be attributed to the decomposition of PET chains.It revealed that all the PETs have similar thermal stabilities.The related thermal characteristic parameters are shown in Table 2.It revealed that four samples display similar values of Tiand Tmax.This phenomenon could be explained that hydrolysis,SE and CS did not undermine the internal structure and crystallinity of PET matrix.
图表编号 | XD0014951900 严禁用于非法目的 |
---|---|
绘制时间 | 2018.12.31 |
作者 | 袁凯、胡祖明、段广宇、于俊荣、王彦、诸静 |
绘制单位 | College of Material Science and Engineering,Donghua University、College of Material Science and Engineering,Donghua University、State Key Laboratory for Modification of Chemical Fibers and Polymer Materials,Donghua University、State Key Laboratory for Modifi |
更多格式 | 高清、无水印(增值服务) |