《Table 1 Characterization of phase composition of precursor powder after heat treatment》
提示：宽带有限、当前游客访问压缩模式
本系列图表出处文件名：随高清版一同展现
《前驱粉粒度对Bi-2223带材微观结构和超导电性的影响研究（英文）》
P.Kameli et al introduce a method to estimate volume fraction of phases，according to X-ray diffraction patterns[9].Volume fractions of phases were estimated by this method to study the effect of particle size on characterization of phase assemblages，as shown in Table 1.Powder 2 has the highestBi-2212 phase content（96.31%）and the lowest Cu O phase content（1.25%）.AEC phase increases from 1.93%to 2.78%with decreasing of particle size.FWHM values of Bi-2212phase（0012）decreases with the decreasing of particle size，which means more sufficient reaction.It can be also concluded that the reaction time of precursor powders decreases with the decrease of particle size.
| 图表编号 | XD0011263200 严禁用于非法目的 |
|---|---|
| 绘制时间 | 2018.09.01 |
| 作者 | 崔利军、张平祥、李金山、闫果、冯勇、刘向宏、李建峰、潘熙峰、张胜楠、马晓波、刘国庆 |
| 绘制单位 | 西北工业大学凝固技术国家重点实验室、西部超导材料科技股份有限公司超导材料制备国家重点实验室、西北工业大学凝固技术国家重点实验室、西部超导材料科技股份有限公司超导材料制备国家重点实验室、西北有色金属研究院、西北工业大学凝固技术国家重点实验室、西部超导材料科技股份有限公司超导材料制备国家重点实验室、西部超导材料科技股份有限公司超导材料制备国家重点实验室、西部超导材料科技股份有限公司超导材料制备国家重点实验室、西部超导材料科技股份有限公司超导材料制备国家重点实验室、西部超导材料科技股份有限公司超导材料制备国家重 |
| 更多格式 | 高清、无水印（增值服务） |