《Table 3The product compositions and TIPB conversion (TOS=5 min) over ZSM‐5 modified by H3PO4 soluti
本系列图表出处文件名:随高清版一同展现
《高硅ZSM-5原粉的外表面改性及其在甲醇制丙烯反应中的应用(英文)》
a Determined by XRF.b Determined by XPS.
Given the higher propene selectivity and longer lifetime observed on ZSM‐5‐P‐1,the H3PO4 concentration in the post‐synthetic treatment was further adjusted to optimize the catalytic performance.The product Si/Al ratios and P contents of the samples are summarized in Table 3.No regular change in the Si/Al ratio can be observed following the increase of H3PO4concentration,and the samples have similar bulk and surface P contents.The insignificant effect of H3PO4 solution on the dealumination of high‐Si as‐made ZSM‐5 is understandable,since high‐Si zeolites are generally acknowledged to be resistant to the acid solution.Indeed,we have carried out post‐synthetic HCl treatment of the same precursor and almost unchanged Si/Al ratios are obtained(Table S2).
图表编号 | XD008192300 严禁用于非法目的 |
---|---|
绘制时间 | 2018.08.01 |
作者 | 赵学斌、洪杨、王林英、樊栋、闫娜娜、刘晓娜、田鹏、郭新闻、刘中民 |
绘制单位 | 大连理工大学化工学院宾州州立大学-大连理工大学联合能源研究中心精细化工国家重点实验室、中国科学院大连化学物理研究所甲醇制烯烃国家工程实验室国家能源低碳催化与工程研发中心洁净能源国家实验室能源材料化学协同创新中心、中国科学院大学、中国科学院大连化学物理研究所甲醇制烯烃国家工程实验室国家能源低碳催化与工程研发中心洁净能源国家实验室能源材料化学协同创新中心、中国科学院大学、中国科学院大连化学物理研究所甲醇制烯烃国家工程实验室国家能源低碳催化与工程研发中心洁净能源国家实验室能源材料化学协同创新中心、中国科学院大连 |
更多格式 | 高清、无水印(增值服务) |