《Table 2 Proportion of non-adherent particles under different outgrowth values and melt delivery tub
提示：宽带有限、当前游客访问压缩模式
本系列图表出处文件名：随高清版一同展现
《双喷嘴气雾化技术制备球形AlSi10Mg粉末及其表征（英文）》
where noutgrowth is the number of outgrowth detected on the particle by using the particle shape analyzer.This formula points out that if a particle surface does not adhere to small particles，the outgrowth value is 0.Similarly，the outgrowth values of 50%，66%，75%or80%，mean that the particle surface adheres to 1，2，3，and 4 small particle（s），respectively.As shown in Table 2，an increase in delivery tube diameter leads to a reduction inadheringparticles，andtheproportionsof non-adherent particles are all above 76%.The powder atomized with a delivery tube diameter of 5.0 mm has the best surface morphology，about 84.86%particles are non-adherent，and only 14.29%，0.83%，0.02%particles adhere 1，2 and 3 small particles，respectively.
| 图表编号 | XD0064474000 严禁用于非法目的 |
|---|---|
| 绘制时间 | 2019.02.01 |
| 作者 | 高超峰、肖志瑜、邹海平、柳中强、陈进、李上奎、张大童 |
| 绘制单位 | 华南理工大学国家金属近净成形工程技术研究中心、华南理工大学广东省金属新材料制备与成形重点实验室、华南理工大学国家金属近净成形工程技术研究中心、华南理工大学广东省金属新材料制备与成形重点实验室、华南理工大学国家金属近净成形工程技术研究中心、江西悦安超细金属有限公司、华南理工大学国家金属近净成形工程技术研究中心、华南理工大学广东省金属新材料制备与成形重点实验室、佛山市岁之博新材料科技有限公司、江西悦安超细金属有限公司、华南理工大学国家金属近净成形工程技术研究中心、华南理工大学广东省金属新材料制备与成形重点实验 |
| 更多格式 | 高清、无水印（增值服务） |