《Table 1.Tensile strength test results for low-carbon steel at room temperature》
提示：宽带有限、当前游客访问压缩模式
本系列图表出处文件名：随高清版一同展现
《Mechanical and corrosion properties of low-carbon steel prepared by friction stir processing》
Fig.5 shows stress–strain curves of the BM，NFSP，and SFSP samples at room temperature，and the tensile strength test results are summarized in Table 1.The ultimate tensile strengths（UTS）of the low-carbon steel increased significantly after NFSP and SFSP，while the elongation to failure（EL）decreased only slightly.The UTS and EL of the BM sample was 470 MPa and 51.4%，respectively.Compared with BM，the UTS of the NFSP and SFSP samples increased by 27.0%and 38.7%，respectively.The ELs of the NFSP and SFSP sample were 47.1%and 45.6%，respectively，which is slightly lower than that of the BM.
| 图表编号 | XD0050012400 严禁用于非法目的 |
|---|---|
| 绘制时间 | 2019.02.01 |
| 作者 | Li-ying Huang、Kuai-she Wang、Wen Wang、Kai Zhao、Jie Yuan、Ke Qiao、Bing Zhang、Jun Cai |
| 绘制单位 | School of Metallurgical Engineering, Xi'an University of Architecture and Technology、National and Local Joint Engineering Research Center for Functional Materials Processing, Xi'an University of Architecture and Technology、School of Metallurgical Engine |
| 更多格式 | 高清、无水印（增值服务） |