《Table 2.Evaluated dislocation densities after different num--bers of passes of TCP m2》
本系列图表出处文件名:随高清版一同展现
《Microstructure evolution of a recycled Al-Fe-Si-Cu alloy processed by tube channel pressing》
Fig.3 compares the morphology,dimensions,and distribution of Al Fe Si intermetallic particles in the microstructure of the used alloy before and after TCP processing.As shown before,these particles usually appear in two different elongated and faceted morphologies[17-19].As evident in Figs.3(a)–3(e),different Al Fe Si particles can be traced in the microstructure of the alloy before and after TCP processing.The chemical compositions of differently numbered particles shown in Fig.3 are presented in Table 1.As can be traced in this table,the chemical composition of these particles is approximately 33wt%Fe,6wt%Si,and 57wt%Al.This chemical composition is very similar to that ofα-Al Fe Si(Al8Fe2Si).As shown in Fig.3(a),three groups of Al Fe Si particles can be traced in the microstructure of the alloy before TCP processing:
图表编号 | XD002879100 严禁用于非法目的 |
---|---|
绘制时间 | 2018.10.01 |
作者 | M.H.Farshidi、M.Rifai、H.Miyamoto |
绘制单位 | Department of Materials Science and Metallurgical Engineering, Ferdowsi University of Mashhad、Department of Mechanical Engineering, Doshisha University、Department of Mechanical Engineering, Doshisha University |
更多格式 | 高清、无水印(增值服务) |