《Table 1.Sample dimensions and final porosity achieved after the sintering process for samples with
提示:宽带有限、当前游客访问压缩模式
本系列图表出处文件名:随高清版一同展现
《Synthesis and characterization of copper foams through a powder metallurgy route using a compressible and lubricant space-holder material》
The foam samples with various acrawax contents(both fine and coarse acrawax)ranging from 40vol%to 70vol%were processed at 300 MPa compaction pressure.Table 1 shows the effect of the added space holder on the final achieved porosity in the cases of both fine and coarse-pore foam samples.The copper foams with finer pores are designated as CF1,CF2,CF3,and CF4 and the coarser-pore foams as CF5,CF6,CF7,and CF8.
图表编号 | XD002876100 严禁用于非法目的 |
---|---|
绘制时间 | 2018.08.01 |
作者 | Mohit Sharma、O.P.Modi、Punit Kumar |
绘制单位 | Department of Mechanical Engineering,National Institute of Technology、CSIR-Advanced Materials & Processes Research Institute、CSIR-Advanced Materials & Processes Research Institute、Department of Material Science & Metallurgical Engineering,Maulana Azad Nat |
更多格式 | 高清、无水印(增值服务) |
查看“Table 1.Sample dimensions and final porosity achieved after the sintering process for samples with various acrawax conte”的人还看了
- 表4 粘结样品与烧结样品的键合拉力对比Table 4 Comparison of the bond pull between the bonded samples and sintered samples
- Table 4–The effect of selected CS molecular weight and concentration on surface porosity%for plain PLGA MPs using double