《Table 3.Fitting results for the EIS of the substrate and cladded coatings》

《Table 3.Fitting results for the EIS of the substrate and cladded coatings》   提示：宽带有限、当前游客访问压缩模式
本系列图表出处文件名：随高清版一同展现
《Wear and corrosion resistance of laser-cladded Fe-based composite coatings on AISI 4130 steel》


  1. 获取 高清版本忘记账户？点击这里登录
  1. 下载图表忘记账户？点击这里登录

The extracted fitting results from the equivalent circuit of the substrate and the cladded coatings are given in Table 3，where Rs is the Na Cl solution resistance，Rct is the charge transfer resistance，and the constant phase element（CPE）Q is used instead of capacitance.The CPE（Q）was calculated with the equation

图表编号XD002873800    严禁用于非法目的
绘制时间2018.06.01
作者Li Fan、Hai-yan Chen、Yao-hua Dong、Li-hua Dong、Yan-sheng Yin
绘制单位College of Ocean Science and Engineering, Shanghai Maritime University、Department of Marine Engineering, Nantong Shipping College、College of Ocean Science and Engineering, Shanghai Maritime University、College of Ocean Science and Engineering, Shanghai Mar
更多格式高清、无水印（增值服务）

相关图表

  1. 《Table 1.Rating scale for adhesion of the coatings》2019.02.01
  2. 《Table 2 Results of the sensitivity analysis and parameter calibration for the SWAT model》2019.03.01
  3. 《Table 4 Evaluation results of the growth and development by z-score for the school children》2019.02.28
  4. 《Table 3–Fitting parameters for the adsorption isotherms of pesticide on illite and kaolinite.》2019.04.15
  5. 《Table 1 DSC results for the glass transition of XNBR and its composites》2019.01.15
  6. 《Table 2 The anatomical results of Group I and II and also shows the additional procedures done for cataract and subluxat》2019.01.18
  7. 《表3 电化学阻抗谱拟合结果 (1.0V) Tab.3 Fitting results of EIS under the condition of 1.0V》2019.01.15
  8. 《Table 1 Conditions for the ADMET polymerization of monomers a and analytical data of the resulting polymers》2018.06.01
  9. 《Table 1 Effect of different dispersion stabilizers on the result of emulsifying and dispersion for polysulfide sealant》2018.02.10
  10. 《Table 3 Curve-fitting results from XPS spectra for O1sof the catalysts*》2018.02.10
  11. 《Table 2:Comparison of the absolutes for the numerical results and absolute errors at point ti=0.0:0.2:1.0 in Example 2》2018.02.15
  12. 《表1 母材及堆焊金属的主要化学成分Tab.1 Chemical composition of the substrate and the clad materials》2018.03.15
  13. 《表3 电化学阻抗拟合结果Table 3 Fitting results of EIS》2018.07.01
  14. 《表4 复合涂层的摩擦磨损结果Table 4 Friction and wear results of the composite coatings》2018.07.25
  15. 《表3 基体与涂层试样浸泡1h的电化学数据Table 3 Electrochemical parameters of the substrate and coating samples immersed for 1h》2018.06.25
  16. 《表6 涂层浸泡不同时间后的电化学阻抗谱拟合结果Table 6 The fitted results for EIS of coating samples with different immerse time》2018.06.25
  17. 《表4 基体与涂层试样的电化学阻抗谱拟合结果Table 4 The fitted results for EIS of substrate and coating samples》2018.06.25
  18. 《表3 不同负向电流密度下制备的微弧氧化膜的EIS谱拟合结果Tab.3 Fitting parameter values for EIS of MAO coating formed at various negative current de》2018.08.20
  19. 《表2 不同镀液添加剂下所得镀层表面的元素分析结果Table 2 Results of elemental analysis for the coatings obtained at different additive volume con》2018.02.01
  20. 《表2 包膜材料配比优化正交试验设计与结果Table 2 Design and results of the orthogonal test for the ratios coating materials》2018.01.30

随机翻阅

《表5 方差分析表：钛铬对低合金赤泥铁组织和性能的影响》 《表2 两组MNSI积分比较(±s)》 《表3 大学生心理危机表现在专业上的差异（N=484)》 《表5 各计算剖面详细信息表》 《表2 两组患者的数据对比》 《表1 呼和浩特地区汉族人群19个STR基因座等位基因及其频率》 《表2 涂料产品主要技术指标》 《表2 火灾热辐射危险性判据》 《表1 引物序列：人羊膜上皮细胞的体外培养及诱导分化》 《表1 样本的地域分布：劳动力转移、模式分异与农户务农收入——基于全国“十县百村”的实证分析》