《Table 3.Contents of Ni and Cu in the matrix and precipitated phase of the Cu-0.4wt%Be-2.1wt%Ni allo
提示:宽带有限、当前游客访问压缩模式
本系列图表出处文件名:随高清版一同展现
《Effects of Ni content on the cast and solid-solution microstructures of Cu-0.4wt% Be alloys》
wt%
EDS was used to analyze the chemical composition of the Cu matrix and the precipitates in the samples with a Ni content of 1.5wt%and 2.1wt%;the results are listed in Table 2.The Ni content in the precipitate was much higher than that in the Cu matrix,indicating that the precipitate was rich in Ni.Notably,the Be atom is too light(atomic number of 4)to be accurately detected using EDS;therefore,the Be content was not quantified in the present work.
图表编号 | XD002871900 严禁用于非法目的 |
---|---|
绘制时间 | 2018.06.01 |
作者 | Shuang-jiang He、Yan-bin Jiang、Jian-xin Xie、Yong-hua Li、Li-juan Yue |
绘制单位 | Key Laboratory for Advanced Materials Processing of Ministry of Education, Institute of Advanced Materials and Technology, University of Science and Technology Beijing、Key Laboratory for Advanced Materials Processing of Ministry of Education, Institute of |
更多格式 | 高清、无水印(增值服务) |
查看“Table 3.Contents of Ni and Cu in the matrix and precipitated phase of the Cu-0.4wt%Be-2.1wt%Ni alloy”的人还看了
- 表1 Cu-Al-Mn-Ti合金的实际合金成分及基体和析出相的化学成分Tab.1 The actual compositions, matrix and precipitated phase chemical compositions of
- 表1 Cu-Al-Mn-Ti合金的实际合金成分及基体和析出相的化学成分Tab.1 The actual compositions, matrix and precipitated phase chemical compositions of