《Table 3.Electrochemical parameters obtained from polarization with Tafel extrapolation for specimen
提示:宽带有限、当前游客访问压缩模式
本系列图表出处文件名:随高清版一同展现
《Azole derivatives embedded in montmorillonite clay nanocarriers as corrosion inhibitors of mild steel》
Finally,the combinations of MMT+MBT and MMT+MBI showed a polarization inhibition efficiency(ηp)of 82%and 75%,respectively,representing the highest and second-highest values,respectively,among the investigated inhibitors.Electrochemical corrosion parameters such as the corrosion potential(Ecorr),corrosion current density(icorr),anodic Tafel slope(ba),and cathodic Tafel slope(bc)were obtained through Tafel extrapolation after the specimens were immersed for 24 h;the results are reported in Table 3.
图表编号 | XD0028410000 严禁用于非法目的 |
---|---|
绘制时间 | 2019.01.01 |
作者 | Milad Edraki、Davood Zaarei |
绘制单位 | Polymer Department, Technical Faculty, South Tehran Branch, Islamic Azad University、Polymer Department, Technical Faculty, South Tehran Branch, Islamic Azad University |
更多格式 | 高清、无水印(增值服务) |
查看“Table 3.Electrochemical parameters obtained from polarization with Tafel extrapolation for specimens of mild steel immer”的人还看了
- Table 4 Adsorption parameters obtained from mass loss measurements for the studied compound in 1 mol/L HCl at different
- Table 2.Obtained electrochemical parameters from EIS tests on the mild steel specimens immersed in the extracted solutio
- 表3 不同p H环境中环氧树脂涂层的极化曲线的拟合电化学参数 (方案B) Tab.3 Electrochemical parameters fitted from polarization curves of coating in envi