《Table 4:Q values for solute elements[35]》

《Table 4:Q values for solute elements[35]》   提示：宽带有限、当前游客访问压缩模式
本系列图表出处文件名：随高清版一同展现
《"Microstructures and tensile properties of as-cast Mg-5Sn-1Si magnesium alloy modified with trace elements of Y, Bi, Sb and Sr"》


  1. 获取 高清版本忘记账户？点击这里登录
  1. 下载图表忘记账户？点击这里登录

Therefore，the refinement mechanism of Y，Bi and Sr elements on Mg-5Sn-1Si magnesium alloy can be explained by both the difference of GRF and the undercooling.For Mg-5Sn-1Si-0.9Sb alloy，the heterogeneous nuclei of Mg3Sb2 phase is the main reason for refinement.

图表编号XD00218893600    严禁用于非法目的
绘制时间2021.01.01
作者He-shuai Yu、Xue-feng Guo、Hong-bao Cui
绘制单位School of Materials Science and Engineering, Henan Polytechnic University、Henan International Joint Research Laboratory for High-Performance Light Metallic Materials and Numerical Simulations,Henan Polytechnic University、School of Materials Science and En
更多格式高清、无水印（增值服务）

相关图表

  1. 《Table 1 Response value of peak area of each wavelength of imidaclothiz standard solution》2018.06.01
  2. 《Table 5 Comparison of ornamental value of carnation cut flower under different solution treatments》2018.02.01
  3. 《Table 4:Summary of magnetostrictive and mechanical properties for third elements or carbides doped Fe-Ga polycrystalline》2020.05.01
  4. 《Table 4:Value the importance of the elements》2019.09.05
  5. 《Table 4:Value the importance of the elements》2019.09.05
  6. 《Table 1 List of morphological characteristics and its function as soil bioengineering elements for slope conservation》2019.03.01
  7. 《Table 2:Electro negativity values and difference of elements[27]》2019.03.01
  8. 《Table 3:Tolerances (wt.%) for trace elements suggested by Gundlach of Element Materials Technology Wixom[13]》2019.03.01
  9. 《Table 6:Mn-equivalent for several elements favoring (+) or preventing (-) pearlite[3]》2019.03.01
  10. 《表1 高碳铬铁冶炼主要元素分配率设定值%Tab.1The set value of major elements allocation rate for high carbon ferrochrome production》2019.02.28
  11. 《Tab.4 p H values of the solutions before and after cleaning for the contaminated fabrics using activated peroxide system》2019.04.22
  12. 《表5 各样本点对应的最优解Table 5 Optimal solution for each sample point》2018.05.28
  13. 《表4 主要溶质元素参数Table 4 Main paramenter of solute elements》2018.07.01
  14. 《表2 同主族元素形成盐的pH Table 2 The pH of salt solution that are formed by different elements with the same main groups》2018.07.02
  15. 《表2 化学镀溶液成分表Table 2 Components of solution for electroless plating》2018.06.01
  16. 《表4 标准溶液荧光值Table 4 Fluorescence value of standard solution》2018.01.15
  17. 《表4 极限粒径的优化解Table 4 Optimal solution of critical CIPs’diameter values》2018.03.15
  18. 《Table 8 Cost analysis for cold forming and hot forming materials solutions》2018.12.30
  19. 《Table 7 Materials solutions for cold forming and hot forming》2018.12.30
  20. 《表2 室温下不同搅拌时间的水泥挤出液pH值Tab.2 pH value of cement extract solution for different stirring time at room temperature》2018.12.20

随机翻阅

《表1 纳入研究基本特征：连花清瘟治疗新型冠状病毒肺炎的系统评价与试验序贯分析》 《表3 不同处理的杂交谷子整株干物质量比较》 《表3 BLEU评估结果：基于特征关联的服装图像特征描述研究》 《表4 女性健康预期寿命及状态转移生存年数分析》 《表1 两组患者实际考核成绩比较[n (%) ]》 《表3 参数设置：区域创新系统中多主体间的动态演化博弈机制及仿真分析》 《表3 超声造影与增强CT检查的诊断结果比较》 《表9 全国省域景气信号灯结果输出》 《表2 两组患者治疗前后肥胖度、体脂百分率、BMI、VFA水平变化情况》 《表1 恶名市场报告中在线市场上榜情况》