《Table 3 Corrosion potential (φcorr) and corrosion current density (Jcorr) of samples A, B, C and D
提示:宽带有限、当前游客访问压缩模式
本系列图表出处文件名:随高清版一同展现
《具有均匀和双峰晶粒尺寸分布的电沉积镍的腐蚀行为(英文)》
Figure 11 shows the potentiodynamic polarization curves for samples A,B,C and D in 3 wt.%NaCl solution,andthecorrespondingelectrochemical parameters are listed in Table 3.It is also apparent tha all samples show a typical active-passive-transpassive corrosion behavior.Similar to that observed in NaOH solution,the corrosion potential of the samples shifts negatively from-0.20 to-0.47 V and the corrosion current density increases from 1.01 to 5.61μA/cm2 with increasing the grain size in the sample.The corrosion resistance decreases with increasing the grain size.
图表编号 | XD0064475700 严禁用于非法目的 |
---|---|
绘制时间 | 2019.02.01 |
作者 | 杨峰、张晓峰、杨虹、刘亦农、郝世杰、崔立山 |
绘制单位 | 中国石油大学(北京)重质油国家重点实验室、中国石油大学(北京)油气装备材料失效与腐蚀防护北京市重点实验室、中国石油大学(北京)重质油国家重点实验室、中国石油大学(北京)油气装备材料失效与腐蚀防护北京市重点实验室、School of Mechanical and Chemical Engineering,The University of Western Australia、School of Mechanical and Chemical Engineering,The University of Wes |
更多格式 | 高清、无水印(增值服务) |
查看“Table 3 Corrosion potential (φcorr) and corrosion current density (Jcorr) of samples A, B, C and D measured in 3 wt.%Na”的人还看了
- Table 5 Corrosion potential (φcorr) and corrosion current density (Jcorr) of samples A, B, C and D measured in 0.5 wt.%H
- Table 1 Corrosion potential (φcorr) , corrosion current density (Jcorr) , passive current density (Jpass) and passive ra
- Table 3 Open circuit potential, corrosion potential (Ecorr) , corrosion current density (Icorr) and corrosion rate value
- 表2 不同质量分数WC/Ni-40%Co熔覆层的自腐蚀电位和自腐蚀电流密度Tab.2 Free corrosion potential and free corrosion current density for WC/Ni-40%Co c