《Table 2 Equivalent circuit parameters determined by modeling impedance spectra of samples A, B, C a
本系列图表出处文件名:随高清版一同展现
《具有均匀和双峰晶粒尺寸分布的电沉积镍的腐蚀行为(英文)》
Figure 9 shows the potentiodynamic polarization curves for as-deposited sample A and heat-treated Ni samples B,C and D in 10 wt.%NaOH solution,respectively.It is immediately apparent that all samples show a typical active-passive-transpassive corrosion behavior,which is related to the formation of Ni(OH)2passive film according to the previous reports[20,32].The corresponding electrochemical parameters extracted from the polarization curves are summarized in Table 1.The corrosion potential shifts negatively from-0.35 to-0.55 V and the corrosion current density increases from0.46 to 3.85μA/cm2 for samples from A to D.These results indicate that the corrosion resistance of the sample decreases with increasing grain size,which is consistent with reported work[12].
图表编号 | XD0064475400 严禁用于非法目的 |
---|---|
绘制时间 | 2019.02.01 |
作者 | 杨峰、张晓峰、杨虹、刘亦农、郝世杰、崔立山 |
绘制单位 | 中国石油大学(北京)重质油国家重点实验室、中国石油大学(北京)油气装备材料失效与腐蚀防护北京市重点实验室、中国石油大学(北京)重质油国家重点实验室、中国石油大学(北京)油气装备材料失效与腐蚀防护北京市重点实验室、School of Mechanical and Chemical Engineering,The University of Western Australia、School of Mechanical and Chemical Engineering,The University of Wes |
更多格式 | 高清、无水印(增值服务) |
查看“Table 2 Equivalent circuit parameters determined by modeling impedance spectra of samples A, B, C and D in 10 wt.%Na OH”的人还看了
- Table 4 Equivalent circuit parameters determined by modeling impedance spectra of samples A, B, C and D in 3 wt.%Na Cl s
- Table 6 Equivalent circuit parameters determined by modeling impedance spectra of samples A, B, C and D in 0.5 wt.%H2SO4