《Table 4:Main technological parameters》
本系列图表出处文件名:随高清版一同展现
《Mixed regulation model of ceramic particles with molten high-chromium iron KmTBCr26》
The microstructure of interface between matrix and ceramic particles is shown in Fig.12.It can be observed with the interface bonding state more clearly.It is found that the particles and the matrix form a\""Class I interface\""(the metal and reinforcements are neither reflected nor dissolved,and the interface is relatively flat)under the experimental parameters in Table 4,which is only mechanical and physical adhesion.This is because the molten metal is non-wetting with ZTA ceramic particles.Under the pressure compositing,the liquid metal is immersed in the rough surface of the ceramic particles to form a mechanical meshing interface on the micro scale which cannot be formed at atmospheric pressure.At the same time,the high temperature preheating of the particles before the mixing improves the activation degree of the particle surface,and also promotes the combination of the interface.
图表编号 | XD0049761100 严禁用于非法目的 |
---|---|
绘制时间 | 2019.03.01 |
作者 | Qi Dong、Shu-ming Xing、Bo Qiu |
绘制单位 | School of Mechanical, Electronic and Control Engineering, Beijing Jiaotong University、School of Mechanical, Electronic and Control Engineering, Beijing Jiaotong University、School of Mechanical, Electronic and Control Engineering, Beijing Jiaotong Universi |
更多格式 | 高清、无水印(增值服务) |