《Shear-thickening behavior of Fe-ZSM5 zeolite slurry and its removal with alumina/boehmites》
Various Fe-ZSM5 zeolite slurries with solid loadings ranging from 50wt%to 70wt%were prepared using a mixer（Speed MixerTM，DAC 150.1 FVZ-K）.To improve the rheology of the slurries，their p H value was adjusted using 0.1mol/L HCl or 0.1 mol/L Na OH solution.The slurries were also mixed with 10wt%halloysite and 10wt%boehmite（Versal 250，Pural SB，or Disperal）while the total solid loading was maintained at 70wt%，as listed in Table 1.The sample code Fe-ZSM5 stands for the corresponding solid composition of 100wt%Fe-ZSM5；the rest codes stand for the solid composition in their corresponding rows（Table 1），where Fe-Z represents Fe-ZSM5，H for halloysite，P for Pural SB，D for Disperal and V for Versal 250.
| 图表编号 | XD002872600 严禁用于非法目的 |
|---|---|
| 绘制时间 | 2018.06.01 |
| 作者 | Xiao-guang Liu、Yan Li、Wen-dong Xue、Jia-lin Sun、Qian Tang |
| 绘制单位 | Department of Inorganic Nonmetallic Materials, School of Materials Science and Engineering, University of Science and Technology Beijing、Department of Inorganic Nonmetallic Materials, School of Materials Science and Engineering, University of Science and |
| 更多格式 | 高清、无水印（增值服务） |