《Table 3.Effect of roasting temperature on the grade and re-covery of nickel and iron》
提示:宽带有限、当前游客访问压缩模式
本系列图表出处文件名:随高清版一同展现
《Feasibility of co-reduction roasting of a saprolitic laterite ore and waste red mud》
wt%
The laterite ore was dried at 80°C for 6 h and then crushed using a laboratory double-roll crusher to pass through 1 mm screen(100wt%).The chemical composition of the saprolitic laterite ore was determined by chemical analysis,as shown in Table 1.The Si O2 and Mg O contents of the ore were high,whereas the iron grade was low.Therefore,the ore was considered to be saprolitic.Fig.1shows the X-ray diffraction(XRD)analysis of the saprolitic laterite ore.
图表编号 | XD002868100 严禁用于非法目的 |
---|---|
绘制时间 | 2018.06.01 |
作者 | Xiao-ping Wang、Ti-chang Sun、Jue Kou、Zhao-chun Li、Yu Tian |
绘制单位 | School of Civil and Resource Engineering, University of Science and Technology Beijing、School of Civil and Resource Engineering, University of Science and Technology Beijing、School of Civil and Resource Engineering, University of Science and Technology Be |
更多格式 | 高清、无水印(增值服务) |
查看“Table 3.Effect of roasting temperature on the grade and re-covery of nickel and iron”的人还看了
- Table 1 Effects of low temperature and poor light storage environments on the morphological indicators of pepper seedlin