《Table 1 Data for characterization of different samples.》
本系列图表出处文件名:随高清版一同展现
《Fabrication of the Core-Shell Structured ZSM-5@Mg(Al)O and Its Catalytic Application in Propane Dehydrogenation》
The data for characterization of different samples are listed in Table 1.As it can be seen that the surface areas of Z@MA-x were greatly decreased as compared with ZSM-5.This phenomenon could be related to the low surface area of Mg Al2O4 in the material.It should be noted that when the Mg(Al)O/ZSM-5 ratio reached up to5,the surface area of Z@MA-5 was reduced significantly to 238 m2/g in distinct contrast with that of Z@MA-1and [email protected] phenomenon could be attributed to the high content of Mg(Al)O shell,which would lead to the pore channel block to some extent in the [email protected],in particular,by the formation of coreshell structure,the Sext of Z@MA-x was significantly increased as compared with that of the pristine ZSM-5,especially for the case of Z@MA-3(209 m2/g).This apparent improvement of structural properties in Z@MA-3 would be propitious to the dispersion of the metals on the support.Based on this good behavior,it is suggested that Z@MA-3 would show a great potential as a catalyst support.
图表编号 | XD0011293700 严禁用于非法目的 |
---|---|
绘制时间 | 2018.03.30 |
作者 | Wang Bo |
绘制单位 | New Product Development Division of Fine Chemicals Company, SINOPEC Yangzi Petrochemical Company Limited |
更多格式 | 高清、无水印(增值服务) |
查看“Table 1 Data for characterization of different samples.”的人还看了
- Table 1 Description of different heat treatments for 49.3 Ti-Ni (at%) wires samples used for properties testing