《Table 2 NH3-TPD and Py-FTIR analyses of the samples》
本系列图表出处文件名:随高清版一同展现
《Synthesis of Core-Shell HZSM-5@SBA-15 Composite and Its Performance in the Conversion of Methanol to Aromatics》
1) Density of the acid sites was assorted according to the acidic type and determined by Py-FTIR.
The NH3-TPD patterns are illustrated in Figure 5.The results for analysis of all catalysts showed two desorption peaks,denoting a low-temperature peak centered around220°C and a high-temperature peak located around 450°C,which were mainly attributed to the weak and strong acid sites,respectively[24].Compared with the pristine HZSM-5,the intensity of desorption peaks for both HZSM-5@SBA-15 and HZSM-5@Si O2 decreased,and such decrease was more apparent for the low temperature peak,which proved the function of the shell capable of reducing the acidity especially the weak acid amounts.The high-temperature peaks of them showed a little shift toward the lower temperature,suggesting a decrease of the strong acid strength.The acid data of samples are listed in Table 2,showing that the amount of weak acid for the core-shell composite decreased by about one half and the strong acid amount decreased by one third.The total acid amount of HZSM-5@SBA-15 is higher than that of HZSM-5@Si O2.
图表编号 | XD0011293200 严禁用于非法目的 |
---|---|
绘制时间 | 2018.03.30 |
作者 | Wang Lu、Li Jian、Wang Lijuan、Chu Shuang、Yang Lina |
绘制单位 | School of Petrochemical Engineering, Liaoning Shihua University、School of Petrochemical Engineering, Liaoning Shihua University、School of Petrochemical Engineering, Liaoning Shihua University、School of Petrochemical Engineering, Liaoning Shihua University |
更多格式 | 高清、无水印(增值服务) |