《Table 1.XRF chemical analysis of the fresh hemimorphite sample》
本系列图表出处文件名:随高清版一同展现
《Improved hemimorphite flotation using xanthate as a collector with S(Ⅱ) and Pb(Ⅱ) activation》
wt%
A high-purity natural hemimorphite(Zn4 (H2O)[Si2O7](OH)2) sample(Yunnan province,China)was used in this study.The chemical composition of the sample was studied by X-ray fluorescence(XRF,Philips X Unique2);the results are shown in Table 1.The sharp and narrow peaks observed in the X-ray diffraction(XRD,Bruker D8 Advance powder diffractometer with Co Kαradiation source)pattern indicate that the hemimorphite sample was pure(Fig.1).Some cubic pieces from the large specimens of hemimorphite were used for contact-angle measurements.The other samples were dry ground with a ceramic mortar and pestle and then screened with stainless steel sieves.The+38 to-106μm size range was used in the microflotation tests,and the<38μm size fraction was further ground in an agate mortar to obtain a particle size of<5μm;this sample was subsequently used in the zeta-potential,SEM–EDS,and DRIFTS measurements.
图表编号 | XD002874100 严禁用于非法目的 |
---|---|
绘制时间 | 2018.08.01 |
作者 | Kai Jia、Qi-ming Feng、Guo-fan Zhang、Qing Shi、Yuan-jia Luo、Chang-bin Li |
绘制单位 | School of Mineral Processing and Bioengineering,Central South University、School of Mineral Processing and Bioengineering,Central South University、School of Mineral Processing and Bioengineering,Central South University、School of Mineral Processing and Bio |
更多格式 | 高清、无水印(增值服务) |
查看“Table 1.XRF chemical analysis of the fresh hemimorphite sample”的人还看了
- Table 1 Comparison on the chemical properties of soil samples cultivated with garden plants for over 3 years and less th