《Table 3.Saturation magnetization values of the auste-nite-containing (BM Ms (c) ) and non-austenite
本系列图表出处文件名:随高清版一同展现
《Effect of retained austenite and nonmetallic inclusions on the thermal/electrical properties and resistance spot welding nuggets of Si-containing TRIP steels》
The XRD patterns are shown in Fig.4.The XRD patterns of the TRIP steels show the corresponding peaks forγandα,which are the main constituents of the steels.The increase in intensity of theγpeaks corresponds to the increase of the RA volume fraction and it appears to increase with increasing Si,Mn,and C contents.The quantitative analysis of the RA volume fractions was calculated with an average error of±0.012%,±0.015%,±0.015%,±0.010%,and±0.014%for steels S1,S2,S3,S4,and S5,respectively,according to the results obtained with the TOPAS software package.Table 2corroborates that the volume fraction of RA increases with increasing content of alloying elements such as Si and Mn.Li et al.[16]reported that a multiphase structure composed of ferrite,bainite,and RA can be obtained via a TRIP heat treatment after cold rolling of steel.Tsukatani et al.[17]found that Si additions greater than 1wt%increase the RA volume fraction by inducing changes in the second phases of bainite and pearlite to bainitic ferrite.
图表编号 | XD0028408900 严禁用于非法目的 |
---|---|
绘制时间 | 2019.01.01 |
作者 | V.H.Vargas、I.Mejía、V.H.Baltazar-Hernández、C.Maldonado |
绘制单位 | Metallurgy and Materials Research Institute, Universidad Michoacana de San Nicolás de Hidalgo, Edificio “U”, Ciudad Universitaria、Metallurgy and Materials Research Institute, Universidad Michoacana de San Nicolás de Hidalgo, Edificio “U”, Ciudad Universit |
更多格式 | 高清、无水印(增值服务) |