《Table 2 Summary of the test results with different widths》
本系列图表出处文件名:随高清版一同展现
《铁基非晶合金带材压磁现象测试与表征方法改进及其压磁特性(英文)》
Note:Ls(0)-inductance initial value,Ls-inductance rangeability,SI-Max-piezomagnetic effect(absolute value),and P-pressure enhancing (sensitive area)
To make a direct observation of the stress sensitivity on the ribbons,we further tested piezomagnetic property of Fe73.5Cu1Nb3Si13.5B9 ribbon with different thickness,which is exhibited in Fig.11.All sets of ribbons present a similar variation:at the beginning of loading,the inductance shows a rapid rising,i.e.the sensitive range,after which,the inductance of the ribbon continue has small changes with the stress increasing,but the variation amplitude is much less than that in the week regime.The sample c with 31~33μm is different,whose inductance value gradually drops with the pressure enhancing after the initial rise,which is called the negative piezomagnetic property.This specific mechanism remains to be further explored.The sensitive range of sample a~d determined by amplification method is0~0.33,0~0.35,0~0.44 and 0~1.20 kPa,respectively.Comprehensive analyses of each sample situation of the piezomagnetic properties are listed in Table 1.
图表编号 | XD0011282200 严禁用于非法目的 |
---|---|
绘制时间 | 2018.11.01 |
作者 | 陈杰、朱正吼、白茹茹、林前英 |
绘制单位 | 南昌大学、南昌大学、南昌大学、南昌大学 |
更多格式 | 高清、无水印(增值服务) |
查看“Table 2 Summary of the test results with different widths”的人还看了
- 表2 不同浓度有机酸盐对大肠杆菌生长影响的正交试验结果Table 2 Orthogonal test result of the inhibitory effect of different concentrations of organi
- 表2 不同脱模剂对粘结强度影响的检测结果 (11层) Table 2 Test results on the impact of different release agents on bond strength (11th floor)