《Table 2 Electrochemical corrosion parameters of Al-Cu-Li alloy weldment in 3.5%Na Cl solution》
提示:宽带有限、当前游客访问压缩模式
本系列图表出处文件名:随高清版一同展现
《时效处理对铝锂合金电子束焊接头耐蚀性能的影响(英文)》
Note:self-corrosion potential,Ecorr;self-corrosion current,Icorr;pitting corrosion potential,Epit;passivation interval,(Epit-Ecorr)
The EXCO is closely related to IGC;it usually develops from pitting corrosion to IGC,and rapidly expands along grain boundary.When the grain boundary is corroded to form corrosion path,the wedge tension will be produced to ambient grains,and it causes tearing of non-corroded parts;the exfoliation occurs in a large area,and even makes alloy break up[4].The morphologies of Al-Cu-Li alloy joint immersed in EXCO solution before and after PWHT are shown in Fig.4.The course of EXCO development of Al-Cu-Li alloy joint is given in Table 1.
图表编号 | XD0011250500 严禁用于非法目的 |
---|---|
绘制时间 | 2018.07.01 |
作者 | 王少刚、黄燕、赵礼 |
绘制单位 | 南京航空航天大学、南京航空航天大学、南京航空航天大学 |
更多格式 | 高清、无水印(增值服务) |
查看“Table 2 Electrochemical corrosion parameters of Al-Cu-Li alloy weldment in 3.5%Na Cl solution”的人还看了
- 表4 不同腐蚀条件下镍基合金718极化曲线参数拟合结果Tab.4 Electrochemical parameters of nickel-base alloy 718at different corrosion conditions
- 表6 镍基合金718在不同温度条件下的电化学参数 (CO2环境) Tab.6 Electrochemical parameters of nickel-base alloy 718at different temperatures (CO2
- Table 5.The intergranular corrosion depth, rank, and exfoliation corrosion rank of the alloy under different conditions