《Table 3 Density of rare-earth composite iron ore tailings ce-ramics》
提示:宽带有限、当前游客访问压缩模式
本系列图表出处文件名:随高清版一同展现
《Rare-earth Cerium Additives for Sinterability of Anorthite-Diopside Ceramics》
When calculating the density of the ceramics,three samples of each group were selected for testing,and the average value of the obtained samples was used to denote the density of the sample.Table 3 shows that the density of C0 is 1.65 g·cm-3,and the value increases with the increase in the content of rare-earth.The increases in the percentages are 1.21%(C3),2.42%(C5),4.85%(C7),5.45%(C9),8.48%(C11),respectively.The results reveal that adding rare-earth Ce is advantageous to the densification sintering of An-Di ceramics.
图表编号 | XD008004500 严禁用于非法目的 |
---|---|
绘制时间 | 2018.06.15 |
作者 | LIU Jie、GAO Zhijian、ZHANG Xiangwen |
绘制单位 | Key Laboratory for Green Chemical Technology of Ministry of Education,School of Chemical Engineering and Technology, Tianjin University、Tianjin Municipal Engineering Design & Research Institute、Key Laboratory for Green Chemical Technology of Ministry of E |
更多格式 | 高清、无水印(增值服务) |