《Table 1.Chemical composition of Cu–Be alloys》
本系列图表出处文件名:随高清版一同展现
《Effects of Ni content on the cast and solid-solution microstructures of Cu-0.4wt% Be alloys》
wt%
The raw materials used in the present work were electrolytic Cu(99.95wt%),Cu-3.5wt%Be master alloy,and electrolytic Ni(99.9wt%).A medium-frequency induction melting furnace was used to produce?100-mm Cu-0.4wt%Be alloy ingots with different Ni contents(0–2.10wt%).The raw materials were melted at 1250°C,and the pouring temperature was 1200°C.The chemical compositions of the alloys were measured;the results are listed in Table 1.Samples with a size of 20 mm(thickness)×60 mm(width)were cut from the alloy ingots and subsequently hot rolled at850°C into sheets with a thickness of 4 mm(referred to as the hot-rolled samples).The hot-rolled samples were cold rolled into sheets with of 2 mm thick(referred to as the cold-rolled samples).
图表编号 | XD002871600 严禁用于非法目的 |
---|---|
绘制时间 | 2018.06.01 |
作者 | Shuang-jiang He、Yan-bin Jiang、Jian-xin Xie、Yong-hua Li、Li-juan Yue |
绘制单位 | Key Laboratory for Advanced Materials Processing of Ministry of Education, Institute of Advanced Materials and Technology, University of Science and Technology Beijing、Key Laboratory for Advanced Materials Processing of Ministry of Education, Institute of |
更多格式 | 高清、无水印(增值服务) |