《Table 3.Theoretical and experimental tensile strength of the SACNT/Ni composites》

《Table 3.Theoretical and experimental tensile strength of the SACNT/Ni composites》   提示：宽带有限、当前游客访问压缩模式
本系列图表出处文件名：随高清版一同展现
《Preparation of super-aligned carbon nanotube-reinforced nickel-matrix laminar composites with excellent mechanical properties》


  1. 获取 高清版本忘记账户？点击这里登录
  1. 下载图表忘记账户？点击这里登录

On the basis of the two aforementioned strengthening mechanisms，the theoretical tensile strength of unidirectional SACNT/Ni composites was predicted.The results are shown in Table 3.

图表编号XD0028411100    严禁用于非法目的
绘制时间2019.01.01
作者Ze-cheng Hou、Lun-qiao Xiong、Yuan-feng Liu、Lin Zhu、Wen-zhen Li
绘制单位School of Materials Science and Engineering, Tsinghua University、School of Materials Science and Engineering, Tsinghua University、School of Materials Science and Engineering, Tsinghua University、Tsinghua-Foxconn Nanotechnology Research Center, Tsinghua Un
更多格式高清、无水印（增值服务）

相关图表

  1. 《表3 劈裂抗拉、抗压强度的试验结果Table 3 Test results of splitting tensile strength and compressive strength》2018.08.25
  2. 《表2 各组试件抗拉承载力计算值与实测值Table 2 Calculation value and measured values of tensile strength of specimens》2018.04.25
  3. 《Table 4:Results and analysis of orthogonal experiment about tensile strength after 4 h》2019.07.01
  4. 《Table 2 Mechanical properties of PEUR-SSx-Ns at original state and after healed:tensile strength (σ) , ultimate elongati》2019.03.01
  5. 《表2 不同储存或使用温度下拉伸强度保持率达到指标临界值的寿命Table 2 Life of tensile strength retention rate reaching the critical value at different s》2018.08.30
  6. 《表2 焊接接头的拉伸性能Table 2 The tensile strength of welded joint》2018.06.25
  7. 《Table 1 Tensile strength and elongation at break of conductive papers containing different PDA-GO content》2018.10.01
  8. 《Table 4 Orthogonal table of tensile strength, bursting strength and tearing strength》2018.04.30
  9. 《表2 3种涂层的拉伸强度和断裂伸长率Table 2 Tensile strength and elongation at break of three coatings》2018.03.30
  10. 《表4 3种复合材料的抗拉伸强度及其Weibull模数Table 4 Tensile strength and Weibull module of BNf/BN, BNf/Si BN and BNf/Si3N4》2018.09.01
  11. 《表4 抗拉强度Table 4 The tensile strength》2018.06.15
  12. 《表2 氧化锡添加量对硅橡胶拉伸强度和剪切强度的影响Table 2 Characteristic tensile strength and shear strength of RTV which filled with Sn O2》2018.06.01
  13. 《表2 原球墨铸铁及强化后材料的抗拉强度Table 2 The tensile strength of the original nodular cast iron and the reinforced material》2018.05.25
  14. 《表2 各检测机构依据ISO-19095测得的Al和Cu与PPS结合体的抗张强度 (MPa) [22]Table 2 Tensile strength (MPa) data of the Al and Cu-PPS joints report》2018.07.10
  15. 《表5 拉应力峰值超过其抗拉极限强度的混凝土单元数量增长率Table 5 The tensile stress peak value exceeds the tensile strength of the concrete unit grow》2018.06.01
  16. 《表3 复合芯棒拉伸强度数据表Table 3 The tensile strength test results of composite core》2018.07.28
  17. 《表2 玻璃纤维拉伸强度测试结果Table 2 The result of glass fiber tensile strength》2018.07.28
  18. 《表2 NOL环试件的实验测试结果Table 2 Experimental strength properties of the NOL tests》2018.05.28
  19. 《表2 试件拉伸强度及修复率Table 2 The tensile strength and recovery rates of specimens》2018.02.28
  20. 《Table 2.Comparison of the strength and ductility values of the multi-layered composite in present study with those from》2018.05.01

随机翻阅

《表1 不同的模拟血型实验比较》 《表2 面板负二项回归模型的估计结果》 《表1 PD流涎症的可能机制》 《表3 无因次应力值及比较》 《表3 建筑构件破拆难点分析》 《表1 三组一般资料比较(±s)》 《表1 2009-2016年妊娠期高血压疾病发生情况[n（%）]》 《表8 3个年份提取结果精度比较》 《表1 miR-21与PTEN的3′UTR互补结合Tab.1 Complementation and combination of miR-21and PTEN 3′UTR》 《表1 不同位置处的狭缝电子运行时间统计》