《硼热/碳热还原技术制备高致密度、高纯度高熵硼化物陶瓷（英文）》


  1. 获取 高清版本忘记账户？点击这里登录
  1. 下载图表忘记账户？点击这里登录
a)According to Reaction（1）；b)according to Reaction（2）.

The grain size was measured from the SEM images.Each reported value was averaged from～400 grains.The modulus and Vickers hardness of the as-sintered ceramics were determined by a mechanical resonance frequencies machine（GrindoSonic，Model MK7，Sweden）and a Vickers Hardness Tester（Durascan50，Struers，Austria），respectively.For the hardness test，hardness values were compared under different loads（0.2，1 and 5 kg）at the same holding time of 15 s.The fracture toughness of HEB was calculated by direct crack measurements according to Anstis equation[43]，based on the crack generated by the indents with a load of 5 kg.A typical indentation image for the crack measurement was shown in Fig.S1.

图表编号XD00110876500    严禁用于非法目的
绘制时间2019.12.01
作者顾俊峰、邹冀、孙世宽、王皓、于苏洋、张金咏、王为民、傅正义
绘制单位State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology、State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology、School of Metallurgy and
更多格式高清、无水印（增值服务）

相关图表

  1. 《Table 3 Sample generation dialog 1》2020.09.01
  2. 《Table 1 Test design》2018.06.01
  3. 《Table 1 Experimental design scheme》2018.12.01
  4. 《表2 结构设计试样表Tab.2 The sample list for structural design》2019.02.01
  5. 《Table 1 Design variables and the design space》2019.05.01
  6. 《Table 1 Studies design》2019.01.18
  7. 《Table 1.Numerical experimental design.》2019.01.10
  8. 《Table 1 Simulated sample separation result》2019.07.01
  9. 《Table 1 Experiment design》2018.02.01
  10. 《Table 1 Design parameter table》2018.09.01
  11. 《表1 年多个样本法和年最大值法暴雨重现期对比Tab.1 Comparison of design return period between multiple sample method and annual maximum method》2018.02.17
  12. 《Table 1 Sample of Standard Generator Characteristics.》2018.08.01
  13. 《表2 基于正交设计的训练样本集Table 2 Training sample set based on orthogonal design》2018.06.30
  14. 《Table 1 Molar contents of each sample》2018.04.10
  15. 《表5 样本电站设计年度电量与2014年生产电量对比Tab.5 Comparison of annual output of sample power station design with 2014production capacity万k》2018.10.20
  16. 《Table 1 Orthogonal experimental design》2018.05.20
  17. 《Table 1 Orthogonal experimental design》2018.05.20
  18. 《Table 1 Sample site and soil characteristics》2018.12.01
  19. 《Table 1 Sintering conditions of each cermet sample》2018.05.01
  20. 《Table 1 Parameters of the sample》2018.04.01

随机翻阅

《表3 德国里斯特养老金免税情况》 《表4 发酵中药渣对断奶仔猪肠道菌群的影响/[Log(copies)/g]》 《表1 2000～2017年西北工业大学研究生创新基金立项基本情况》 《表6 硬度测试结果2：某型装甲车用履带断裂分析》 《表3 杨小舟蛾第4代各期Ki值与总K值回归系数》 《表1 支架和后挡泥板材料参数》 《表3 HBeAg阴转影响因素多因素COX分析结果》 《表3:社会阶级对德国各政党的支持细目分类 (%)》 《表4 NEWS评分内容》 《表2 各药物单用及联用终浓度》