《Table 1 Te xtural prope rtie s and re lative crystallinity of the H-ZSM-5 ze olite s with diffe re

  提示：宽带有限、当前游客访问压缩模式

本系列图表出处文件名：随高清版一同展现

《H-ZSM-5分子筛硅铝比对其催化的甲醇转化丙烯选择性的影响（英文）》

1. 获取 高清版本忘记账户？点击这里登录

1. 下载图表忘记账户？点击这里登录

a:surface area was obtained by the BET method；the micropore surface area and volume were determined by the t-plot method；total pore volume w as estimated from the nitrogen adsorption at p/p0=0.99；the external surface area and mesopore volume w ere the dif

Figure 1 show s the XRD patterns of H-ZSM-5zeolites；all the synthesized samples display the typical diffraction peaks of intrinsic M FI structure.Taking HZ-5（4000）zeolite as a reference，they all havearelativecrystallinityof90%-100%，demonstrating their highly crystalline M FI structure.The textural properties determined from the nitrogen adsorption-desorption isotherms are summarized in Table 1；all the synthesized H-ZSM-5 samples have a similar BET surface area（415-430 m2/g）and micro surface area（306-341 m2/g），as w ell as almost the same pore volume（0.20 cm3/g）and micropore volume（0.15 cm3/g）.In addition，as estimated by Scherrer’s method from the diffraction peak of（011）plane at 7.9°，all the as-synthesized samples have a similar crystal size of 66-73 nm（Table 1）.