《Table 3 Zr-4 alloy and Sample 4 in 1 200C steam environment for 1 h》
提示:宽带有限、当前游客访问压缩模式
本系列图表出处文件名:随高清版一同展现
《Microstructure and corrosion resistance of sputtered TiN coatings on surface of Zr-4 alloy》
The total pressure was about 0.5 Pa.To perform the sputtering process in a nitrogen rich environment,the flow rate of Ar was maintained at 40 cm3/min,and the flow rate of N2 ranged from 0 to 10 cm3/min.The specific synthesis conditions are summarized in Table1.
图表编号 | XD0011320600 严禁用于非法目的 |
---|---|
绘制时间 | 2018.03.01 |
作者 | 廖帮亮、MA Jian-guang、ZHU Wei-hua、ZHU Hong-mei、YANG Kai、LIU Yan-hong、LI Huai-lin、WANG Xiao-jing、王新林 |
绘制单位 | School of Mechanical Engineering, University of South China、School of Mechanical Engineering, University of South China、School of Electrical Engineering, University of South China、School of Mechanical Engineering, University of South China、School of Mecha |
更多格式 | 高清、无水印(增值服务) |
查看“Table 3 Zr-4 alloy and Sample 4 in 1 200C steam environment for 1 h”的人还看了
- Table 2 Variation in crystallite size and lattice strain of as-milled and sintered alloy obtained using Williamson-Hall