《Tab.2Chloride ion diffusion coefficients of concrete after dif- ferent curing regimes》

《Tab.2Chloride ion diffusion coefficients of concrete after dif- ferent curing regimes》   提示：宽带有限、当前游客访问压缩模式
本系列图表出处文件名：随高清版一同展现
《二次水养护对蒸压混凝土长期强度与耐久性能的影响（英文）》


  1. 获取 高清版本忘记账户？点击这里登录
  1. 下载图表忘记账户？点击这里登录
10-9cm2/s

Due to the beneficial effects of SW curing，the chloride diffusion coefficients of concrete after steam-autoclave+SW curing were reduced，and the improvements became more obvious with testing age.Corresponding to the age of360 d，the chloride diffusion coefficient of concrete after steam-autoclave+SW curing dropped to 0.58 times of that after steam-autoclave curing.Therefore，SW curing can lengthen the predicted service life of steam-autoclaved concrete members even when exposed to a harsh marine environment.

图表编号XD0015632700    严禁用于非法目的
绘制时间2018.12.01
作者李果、高祥
绘制单位中国矿业大学深部岩土力学与地下工程国家重点实验室、中国矿业大学深部岩土力学与地下工程国家重点实验室
更多格式高清、无水印（增值服务）

相关图表

  1. 《Tab.2 Diffusion coefficients of N-AEmS/TTAB (m=3, 5, 7, 9) (1.0×10-3 mol/L)》2019.08.22
  2. 《Table 2.Diffusion coefficients at 1300°C of elements in the present alloy and those reported for other Co-based alloy sy》2019.02.01
  3. 《Table 3.Partition coefficients and diffusion coefficient of solute in interstitial-free molten steel》2019.02.01
  4. 《Table 2 Comparing calculational and experimental results[8]of diffusion coefficient》2019.02.01
  5. 《Table 2 Distribution Coefficients of the recycled M[H]-11.9 lithium ion-sieve membrane》2019.03.01
  6. 《表3 MKPC试件在三种环境下硫酸盐腐蚀时间和硫酸根离子扩散深度Tab.3 Sulfate corrosion time and sulfate ion diffusion depth of MKPC specimen in three e》2019.01.01
  7. 《Table 4.Values of regression coefficients (R2) and diffusion coefficient (De)》2019.01.01
  8. 《Table 4 Dataset of diffuse attenuation coefficient at 490 nm(AttachFile1.xlsx)》2017.06.29
  9. 《表7 不同规模企业动态能力Kendall相似系数检验Tab.7 Test of Kendall′s coefficient of concordance for enterprises in different scales》2018.05.20
  10. 《表2 不同次数冻融循环下混凝土氯离子扩散系数Table 2 The chloride diffusion coefficients of specimens after different FT cycles》2018.06.28
  11. 《表3 25℃时不同浓度CGS-12的表观扩散系数Tab.3 Apparent diffusion coefficient for different concentrations of CGS-12at 25℃》2018.04.01
  12. 《表2 用计时电势法得到不同温度下不同[F-]/[Th (IV) ]比值时Th (IV) 的扩散系数Table 2 Diffusion coefficients of Th (IV) at different temperatures obt》2018.06.20
  13. 《表1 扩散系数的测量结果Tab.1 Measured results of diffusion coefficient》2018.08.25
  14. 《Tab.3 Carbonation coefficients of concrete after different curing regimes》2018.12.01
  15. 《Tab.4 MIP results of concrete after different curing regimes》2018.12.01
  16. 《表4 侧壁材料漫反射系数Table 4 Diffuse reflection coefficient of different sidewall materials》2018.03.01
  17. 《表2 利用CV测得的锂离子电池电极材料中锂离子扩散系数[25]Table 2 Li-ion diffusion coefficient of Li-ion battery electrode materials obtained using》2018.05.01
  18. 《Table 1Acidic properties of ZSM‐35 zeolites after sodium ion‐exchange treat‐ment.》2018.11.01
  19. 《Table 1 Thermal diffusion coefficients of two samples》2018.08.01
  20. 《表3 OH-离子在GMZ膨润土中的弥散系数Table 3 The diffusivity of hydroxide ions in GMZ bentonite》2018.04.01

随机翻阅

《表2 海洋浪溅区暴露700 d不同裂缝宽度混凝土中钢筋脱钝时间及腐蚀速率》 《表1：概念化列表（部分）》 《表4 两组治疗前后HAMA和HAMD评分比较（分，±s)》 《表1 仪器测量条件：X射线荧光光谱法测定硬质合金高钴、高镍残次料中钴、镍、铬、铁量》 《表1：用途广泛的分式方程》 《表1 具有手写功能的应用程序市场调查》 《表2 正则化粒子滤波算法》 《表4《经籍考》经部引用六部主要书目之情况一览表》 《表1 犊山水利枢纽生态调水固定资产折旧计算结果》 《表2 TGA主要参数与常规凝血功能检测》