《Table 4 Mechanical properties of AZ31 magnesium alloy under different DCT conditions》
本系列图表出处文件名:随高清版一同展现
《轧前深冷处理对AZ31镁合金显微组织和力学性能的影响(英文)》
The experimental material was as-cast AZ31 magnesium alloy.The alloy’s main chemical composition and content used in the experiment is shown in Table 1.Samples of 100 mm in length,100 mm in width,and 10 mm in thickness were cut from the as-cast alloy and then directly subjected to cryogenic treatment.The cryogenic treatment experimental process was accomplished by placing the specimens in a closed chamber containing the cryogenic medium liquid nitrogen.After cryogenic treatment,the samples were frozen to room temperature in the cryogenic chamber.The experimental scheme is shown in Table 2.After cryogenic treatment,the specimens were then rolled by an experimental two-high laboratory mill(320 mm diameter and 340 mm length),and the rolling speed was 0.2 m/s.All the specimens were rolled to 5.5mm thickness with the same reduction.
图表编号 | XD0011271900 严禁用于非法目的 |
---|---|
绘制时间 | 2018.10.01 |
作者 | 黄志权、韦建春、黄庆学、马立峰、高翔宇、岳照涵 |
绘制单位 | 太原科技大学重型机械教育部工程研究中心、广西柳州钢铁集团有限公司、太原科技大学重型机械教育部工程研究中心、太原科技大学重型机械教育部工程研究中心、太原科技大学重型机械教育部工程研究中心、太原科技大学重型机械教育部工程研究中心 |
更多格式 | 高清、无水印(增值服务) |
查看“Table 4 Mechanical properties of AZ31 magnesium alloy under different DCT conditions”的人还看了
- 表1 不同应变速率下AZ31镁合金变形后晶粒尺寸 (μm) Tab.1 Grain size of deformed AZ31 magnesium alloy under different strain rates (μm)
- 表3 不同浇注工艺参数下AZ91镁合金的晶粒尺寸测量值Tab.3 Measured values of grain size of AZ91 magnesium alloy under different pouring process p