《Table 1 Nominal composition of GH586 superalloy(wt%)》
提示:宽带有限、当前游客访问压缩模式
本系列图表出处文件名:随高清版一同展现
《粉末包埋法制备镍基高温合金Al-Cr-Y涂层的高温氧化行为(英文)》
The substrate of the coated specimens was a GH586 superalloy with nominal composition shown in Table 1,and the specimens were standard heat treated and mainly composed of theγmatrix and theγ′phase[15].The specimens were cut to dimensions of approximately 10 mm×10 mm×5 mm by electro-discharge machining and manually ground with abrasive paper to a 1500 grit finish.Then,the specimens were further polished,ultrasonically degreased,and cleaned in acetone before the pack cementation process.